Poly(vinyl acetal) resin compositions, layers, and interlayers having enhanced optical properties

ABSTRACT

Resin compositions, layers, and interlayers comprising two or more thermoplastic polymers and at least one RI balancing agent for adjusting the refractive index of at least one of the resins or layers is provided. Such compositions, layers, and interlayers exhibit enhanced optical properties while retaining other properties, such as impact resistance and acoustic performance.

CROSS-REFERENCE TO RELATED APPLICATION

This application claims priority to U.S. Provisional Application Ser. No. 62/088,953 filed Dec. 8, 2014, the disclosure of which is incorporated herein by reference in its entirety.

BACKGROUND

1. Field of the Invention

This disclosure relates to polymer resins and, in particular, to polymer resins suitable for use in polymer interlayers, including those utilized in multiple layer panels.

2. Description of Related Art

Poly(vinyl butyral) (PVB) is often used in the manufacture of polymer sheets that can be used as interlayers in multiple layer panels, including, for example, light-transmitting laminates such as safety glass or polymeric laminates. PVB is also used in photovoltaic solar panels to encapsulate the panels which are used to generate and supply electricity for commercial and residential applications.

Safety glass generally refers to a transparent laminate that includes at least one polymer sheet, or interlayer, disposed between two sheets of glass. Safety glass is often used as a transparent barrier in architectural and automotive applications, and one of its primary functions is to absorb energy resulting from impact or a blow without allowing penetration of the object through the glass and to keep the glass bonded even when the applied force is sufficient to break the glass. This prevents dispersion of sharp glass shards, which minimizes injury and damage to people or objects within an enclosed area. Safety glass may also provide other benefits, such as a reduction in ultraviolet (UV) and/or infrared (IR) radiation, and it may also enhance the aesthetic appearance of window openings through addition of color, texture, and the like. Additionally, safety glass with desirable acoustic properties has also been produced, which results in quieter internal spaces.

Often, polymers that exhibit one set of desirable properties, such as acoustic performance, lack other desirable properties, such as impact resistance or strength. Therefore, in order to achieve desirable combinations of properties, multilayered polymer interlayers have been used. These multilayered interlayers may include at least one inner “core” layer sandwiched between two outer “skin” layers. Often, the core layer of an interlayer may be a softer layer having a lower glass transition temperature, which enhances its acoustic performance. However, because such resin layers can be difficult to easily process and/or transport, the skin layers of such multilayered interlayers are often stiffer, with higher glass transition temperatures, which imparts enhanced processability, strength, and impact resistance to the interlayer.

However, use of various layers having different properties can also produce optical defects within the interlayer. For example, one defect common to these types of multilayer interlayers is mottle. Mottle is an objectionable form of optical distortion or visual defect appearing as uneven spots or texture, usually in the final structure. Mottle is caused by small-scale surface variations at the interfaces between the soft and stiff layers wherein the individual layers have different refractive indices. Clarity is another important optical property that is determined by measuring the level of haze within the interlayer or panel. High haze typically occurs when different types of optically incompatible polymers and/or plasticizers are blended or mixed together. In such mixtures, light passing through the blend is scattered as it encounters regions of different polymer materials, and the result is a hazy, visually unclear appearance. High clarity polymers and interlayers are those having very low haze values.

Thus, a need exists for polymer resins, resin layers, and interlayers that exhibit desirable optical properties, such as reduced haze and mottle and improved clarity, without sacrificing other properties, including impact resistance and acoustic performance. Such interlayers could be monolithic or multilayered and should be usable in a wide variety of applications, including safety glass and polymer laminates.

SUMMARY

In a first embodiment, the present invention is a blended resin composition comprising: a first poly(vinyl acetal) resin component comprising a residual hydroxyl content; a second poly(vinyl acetal) resin component comprising a residual hydroxyl content; and at least one high RI plasticizer; wherein there is at least a 2 weight percent difference in the residual hydroxyl content between said first poly(vinyl acetal) resin and said second poly(vinyl acetal) resin.

In a second embodiment, the present invention is a composition comprising: a blended poly(vinyl acetal) resin comprising: a first poly(vinyl acetal) resin comprising a residual hydroxyl content; a second poly(vinyl acetal) resin comprising a residual hydroxyl content; and at least one high RI plasticizer, wherein the plasticizer has a refractive index of at least 1.460, wherein the refractive index of said blended poly(vinyl acetal) resin is at least 1.480; and wherein there is at least a 2 weight percent difference in the residual hydroxyl content between said first poly(vinyl acetal) resin and said second poly(vinyl acetal) resin.

In a third embodiment, the present invention is a method for making an interlayer, said method comprising: (a) providing a first poly(vinyl acetal) resin or resin precursor comprising a residual hydroxyl content; (b) providing a second poly(vinyl acetal) resin or resin precursor comprising a residual hydroxyl content; (c) blending said first poly(vinyl acetal) resin or resin precursor and said second poly(vinyl acetal) resin or resin precursor and a high RI plasticizer to provide a blended plasticized poly(vinyl acetal) resin; and (d) forming at least one resin layer comprising said blended plasticized poly(vinyl acetal) resin; wherein there is at least a 2 weight percent difference in the residual hydroxyl content between said first poly(vinyl acetal) resin and said second poly(vinyl acetal) resin.

DETAILED DESCRIPTION

Resin compositions, layers, and interlayers according to various embodiments of the present invention can comprise one or more thermoplastic polymers and a refractive index (RI) balancing agent. As used herein, the term “refractive index balancing agent” or “RI balancing agent” refers to any component or additive included in the composition, layer, or interlayer for adjusting the refractive index of at least one of the resins or layers. The RI balancing agent may increase or reduce the refractive index of at least one of the resins or layers within an interlayer, which may improve the optical properties of the interlayer, including mottle, haze, and/or clarity, as compared to an identical interlayer formed without an RI balancing agent.

As used herein, the terms “polymer resin composition” and “resin composition” refer to compositions including one or more polymer resins. Polymer compositions may optionally include other components, such as plasticizers and/or other additives. As used herein, the terms “polymer resin layer” and “resin layer” refer to one or more polymer resins, optionally combined with one or more plasticizers, that have been formed into a polymeric sheet. Again, resin layers can include additional additives, although these are not required. As used herein, the term “interlayer” refers to a single or multiple layer polymer sheet suitable for use with at least one rigid substrate to form a multiple layer panel. The terms “single-sheet” interlayer and “monolithic” interlayer refer to interlayers formed of one single resin sheet, while the terms “multiple layer” and “multilayer” interlayer refer to interlayers having two or more resin sheets coextruded, laminated, or otherwise coupled to one another.

The resin compositions, layers, and interlayers described herein may include one or more thermoplastic polymers. Examples of suitable thermoplastic polymers can include, but are not limited to, poly(vinyl acetal) resins, polyurethanes (PU), poly(ethylene-co-vinyl) acetates (EVA), polyvinyl chlorides (PVC), poly(vinylchloride-co-methacrylate), polyethylenes, polyolefins, ethylene acrylate ester copolymers, poly(ethylene-co-butyl acrylate), silicone elastomers, epoxy resins, and acid copolymers such as ethylene/carboxylic acid copoloymers and ionomers thereof, derived from any of the previously-listed polymers, and combinations thereof. In some embodiments, the thermoplastic polymer can be selected from the group consisting of poly(vinyl acetal) resins, polyvinyl chloride, and polyurethanes, or the resin can comprise one or more poly(vinyl acetal) resins. Although described herein with respect to poly(vinyl acetal) resins, it should be understood that one or more of the above polymer resins could be included with, or in the place of, the poly(vinyl acetal) resins described below in accordance with various embodiments of the present invention.

When the resin compositions, layers, and interlayers described herein include poly(vinyl acetal) resins, the poly(vinyl acetal) resins can be formed according to any suitable method. Poly(vinyl acetal) resins can be formed by acetalization of polyvinyl alcohol with one or more aldehydes in the presence of an acid catalyst. The resulting resin can then be separated, stabilized, and dried according to known methods such as, for example, those described in U.S. Pat. Nos. 2,282,057 and 2,282,026, as well as “Vinyl Acetal Polymers,” in the Encyclopedia of Polymer Science & Technology, 3^(rd) ed., Volume 8, pages 381-399, by B. E. Wade (2003). The resulting poly(vinyl acetal) resins may have a total percent acetalization of at least about 50, at least about 60, at least about 70, at least about 75, at least about 80, at least about 85 weight percent, measured according to ASTM D-1396, unless otherwise noted. The total amount of aldehyde residues in a poly(vinyl acetal) resin can be collectively referred to as the acetal component, with the balance of the poly(vinyl acetal) resin being residual hydroxyl and residual acetate groups, which will be discussed in further detail below.

According to some embodiments, the resin composition, layer, or interlayer may include at least one poly(vinyl acetal) resin, which may be present in the composition, layer, or interlayer in an amount of at least about .3 percent, at least about 0.5, at least about 1, at least about 2, at least about 3, at least about 5, at least about 10, at least about 15, at least about 20, at least about 30, at least about 40, or at least about 45 weight percent, based on the combined weight of all resins in the composition, layer, or interlayer. Together, the at least one poly(vinyl acetal) resins can make up at least about 10, at least about 20, at least about 30, at least about 40, at least about 50, at least about 60, at least about 70, or at least about 80 weight percent of composition, layer, or interlayer, based on the combined weight of all resins. In some embodiments, the amount of resins other than the at least one poly(vinyl acetal) resin can be not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 2, or not more than about 1 weight percent, based on the combined weight of all resins.

In some embodiments, the resin composition, layer, or interlayer can include at least a first poly(vinyl acetal) resin and a second poly(vinyl acetal) resin, each of which may be present in the composition, layer, or interlayer in an amount of at least about 0.5, at least about 1, at least about 2, at least about 3, at least about 5, at least about 10, at least about 15, at least about 20, at least about 30, at least about 40, or at least about 45 weight percent, based on the combined weight of all resins in the composition, layer, or interlayer. Together, the first and second poly(vinyl acetal) resins can make up at least about 10, at least about 20, at least about 30, at least about 40, at least about 50, at least about 60, at least about 70, or at least about 80 weight percent of composition, layer, or interlayer, based on the combined weight of all resins. In some embodiments, the amount of resins other than the first and second poly(vinyl acetal) resins can be not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 2, or not more than about 1 weight percent, based on the combined weight of all resins.

In some embodiments, one of the first and the second poly(vinyl acetal) resins can be present in the composition, layer, or interlayer in an amount of less than 12 weight percent, based on the combined weight of the first and second poly(vinyl acetal) resins. For example, the first or the second poly(vinyl acetal) resin can be present in the composition, layer, or interlayer in an amount of at least about 0.5, at least about 1, at least about 1.5, at least about 2, at least about 2.5, at least about 3, at least about 3.5, at least about 4, at least about 4.5, at least about 5, at least about 5.5, at least about 6, at least about 6.5, at least about 7 weight percent and/or not more than about 12, not more than about 11.5, not more than about 11, not more than about 10.5, not more than about 10, not more than about 9.5, not more than about 9, not more than about 8.5, not more than about 8, not more than about 7.5 weight percent, based on the combined weight of the first and second poly(vinyl acetal) resins. In some embodiments, one of the first and second poly(vinyl acetal) resins can be present in the composition, layer, or interlayer in an amount in the range of from about 0.5 to about 12, about 1.5 to about 11.5, about 2 to about 11, about 2.5 to about 10 weight percent, based on the combined weight of the first and second poly(vinyl acetal) resins.

The first and second poly(vinyl acetal) resins can include residues of any suitable aldehyde and, in some embodiments, can include residues of at least one C₁ to C₁₀ aldehyde, at least one C₄ to C₈ aldehyde. Examples of suitable C₄ to C₈ aldehydes can include, but are not limited to, n-butyraldehyde, iso-butyraldehyde, 2-methylvaleraldehyde, n-hexyl aldehyde, 2-ethylhexyl aldehyde, n-octyl aldehyde, and combinations thereof. At least one of the first and second poly(vinyl acetal) resins can include at least about 20, at least about 30, at least about 40, at least about 50, at least about 60, or at least about 70 weight percent of residues of at least one C₄ to C₈ aldehyde, based on the total weight of aldehyde residues of the resin, and/or can include not more than about 90, not more than about 85, not more than about 80, not more than about 75, not more than about 70, or not more than about 65 weight percent of at least one C₄ to C₈ aldehyde, or in the range of from about 20 to about 90, about 30 to about 80, or about 40 to about 70 weight percent of at least one C₄ to C₈ aldehyde. The C₄ to C₈ aldehyde may be selected from the group listed above, or it can be selected from the group consisting of n-butyraldehyde, iso-butyraldehyde, 2-ethylhexyl aldehyde, and combinations thereof.

In various embodiments, the first and/or second poly(vinyl acetal) resin may be a polyvinyl n-butyral (PVB) resin. In other embodiments, the first and/or second poly(vinyl acetal) resin can be a poly(vinyl n-butyral) resin that mainly comprises residues of n-butyraldehyde, and may, for example, include not more than about 50, not more than about 40, not more than about 30, not more than about 20, not more than about 10, not more than about 5, or not more than about 2 weight percent of residues of an aldehyde other than n-butyraldehyde, based on the total weight of all aldehyde residues of the resin. When the first and/or second poly(vinyl acetal) resins are PVB resins, the molecular weight of the resins can be at least about 50,000, at least about 70,000, at least about 100,000 Daltons and/or not more than about 600,000, not more than about 550,000, not more than about 500,000, not more than about 450,000, or not more than 425,000 Daltons, measured by size exclusion chromatography using low angle laser light scattering (SEC/LALLS) or UV/differential refractometer detectors. As used herein, the term “molecular weight” refers to weight average molecular weight (M_(w)). The molecular weight of the first and/or second poly(vinyl acetal) resin can be in the range of from about 50,000 to about 600,000, about 70,000 to about 450,000, or about 100,000 to about 425,000 Daltons.

Although generally described herein with respect to first and second poly(vinyl acetal) resins, it should be understood that, in some embodiments, an equivalent single poly(vinyl acetal) resin including first and second acetal moieties may be substituted for the first and second poly(vinyl acetal) resins with similar results. As used herein, the term “poly(vinyl acetal) resin component” can refer to an individual poly(vinyl acetal) resin present in a blend of resins or to an acetal moiety present on a single poly(vinyl acetal) resin. In various embodiments, the ratio, by weight, of the amount of the first poly(vinyl acetal) resin component to the second poly(vinyl acetal) resin component in a layer, interlayer, or blend can be in the range of from about 0.5:99.5 to about 99.5:0.5, about 1:99 to 99:1, about 10:90 to about 90:10, about 25:75 to about 75:25, or about 40:60 to about 60:40.

In some embodiments, at least one resin composition, layer, or interlayer can include at least a first poly(vinyl acetal) resin component and a second poly(vinyl acetal) resin component. In some embodiments, the first and second resin components may comprise first and second poly(vinyl acetal) resins that can be physically mixed to form a resin blend, which may be combined with one or more plasticizers or other additives to provide a blended resin layer or interlayer. In other embodiments, the first and second poly(vinyl acetal) resin components may be present as respective first and second acetal moieties in a single poly(vinyl acetal) resin. As with the resin blend, this single “hybrid” poly(vinyl acetal) resin can be optionally blended with a plasticizer and utilized in resin layers and interlayers.

In some embodiments, when the resin components include poly(vinyl acetal) resins, the first and second poly(vinyl acetal) resins may be blended such that one of the first and second resins is dispersed within the other of the first and second resins, which can form domains of one of the first and second poly(vinyl acetal) resins within the other of the first and second poly(vinyl acetal) resins. Such a blended resin may be used as a single layer interlayer or it may be combined with one or more adjacent layers to form a multilayer interlayer. In other embodiments, the first and second poly(vinyl acetal) resins can be present in adjacent layers of a multilayer interlayer, such that one of the layers of the interlayer includes the first poly(vinyl acetal) resin and another layer of the interlayer includes the second poly(vinyl acetal) resin. Additional layers can also be present adjacent to at least one of the layers.

The resin compositions, layers, and interlayers according to various embodiments of the present invention can further include at least one plasticizer. Depending on the specific composition of the resin or resins in a composition, layer, or interlayer, the plasticizer may be present in an amount of at least about 5, at least about 10, at least about 15, at least about 20, at least about 25, at least about 30, at least about 35, at least about 40, at least about 45, at least about 50, at least about 55, at least about 60 parts per hundred parts of resin (phr) and/or not more than about 120, not more than about 110, not more than about 105, not more than about 100, not more than about 95, not more than about 90, not more than about 85, not more than about 75, not more than about 70, not more than about 65, not more than about 60, not more than about 55, not more than about 50, not more than about 45, or not more than about 40 phr, or in the range of from about 5 to about 120, about 10 to about 110, about 10 to about 100, about 20 to about 90, or about 25 to about 75 phr. Specific embodiments are discussed in detail shortly.

As used herein, the term “parts per hundred parts of resin” or “phr” refers to the amount of plasticizer present as compared to one hundred parts of resin, on a weight basis. For example, if 30 grams of plasticizer were added to 100 grams of a resin, the plasticizer would be present in an amount of 30 phr. If the resin composition, layer, or interlayer includes two or more resins, the weight of plasticizer is compared to the combined amount of all resins present to determine the parts per hundred resin. Further, when the plasticizer content of a layer or interlayer is provided herein, it is provided with reference to the amount of plasticizer in the mix or melt that was used to produce the layer or interlayer.

Examples of suitable plasticizers can include, but are not limited to, triethylene glycol di-(2-ethylhexanoate) (“3GEH”), triethylene glycol di-(2-ethylbutyrate), triethylene glycol diheptanoate, tetraethylene glycol diheptanoate, tetraethylene glycol di-(2-ethylhexanoate) (“4GEH”), dihexyl adipate, dioctyl adipate, hexyl cyclohexyladipate, diisononyl adipate, heptylnonyl adipate, di(butoxyethyl) adipate, and bis(2-(2-butoxyethoxy)ethyl) adipate, dibutyl sebacate, dioctyl sebacate, and mixtures thereof. The plasticizer may be selected from the group consisting of triethylene glycol di-(2-ethylhexanoate) and tetraethylene glycol di-(2-ethylhexanoate), or the plasticizer can comprise triethylene glycol di-(2-ethylhexanoate).

According to some embodiments, the first and second poly(vinyl acetal) resins in the compositions, layers, and interlayers described herein can have different compositions. For example, in some embodiments, the first poly(vinyl acetal) resin can have a residual hydroxyl content and/or residual acetate content that is at least about 2, at least about 3, at least about 4, at least about 5, at least about 6, or at least about 8 weight percent higher or lower than the residual hydroxyl content and/or residual acetate content of the second poly(vinyl acetal) resin. As used herein, the terms “residual hydroxyl content” and “residual acetate content” refer to the amount of hydroxyl and acetate groups, respectively, that remain on a resin after processing is complete. For example, polyvinyl n-butyral can be produced by hydrolyzing polyvinyl acetate to polyvinyl alcohol, and then acetalizing the polyvinyl alcohol with n-butyraldehyde to form polyvinyl n-butyral. In the process of hydrolyzing the polyvinyl acetate, not all of the acetate groups are converted to hydroxyl groups, and residual acetate groups remain on the resin. Similarly, in the process of acetalizing the polyvinyl alcohol, not all of the hydroxyl groups are converted to acetal groups, which also leaves residual hydroxyl groups on the resin. As a result, most poly(vinyl acetal) resins include both residual hydroxyl groups (as vinyl hydroxyl groups) and residual acetate groups (as vinyl acetate groups) as part of the polymer chain. The residual hydroxyl content and residual acetate content are expressed in weight percent, based on the weight of the polymer resin, and are measured according to ASTM D-1396, unless otherwise noted.

The difference between the residual hydroxyl content of the first and second poly(vinyl acetal) resins could also be at least about 2, at least about 5, at least about 10, at least about 12, at least about 15, at least about 20, or at least about 30 weight percent. As used herein, the term “weight percent different” or “the difference is at least weight percent” refers to a difference between two given weight percentages, calculated by subtracting the one number from the other. For example, a poly(vinyl acetal) resin having a residual hydroxyl content of 12 weight percent has a residual hydroxyl content that is 2 weight percent lower than a poly(vinyl acetal) resin having a residual hydroxyl content of 14 weight percent (14 weight percent−12 weight percent=2 weight percent). As used herein, the term “different” can refer to a value that is higher than or lower than another value.

At least one of the first and second poly(vinyl acetal) resins can have a residual hydroxyl content of at least about 14, at least about 14.5, at least about 15, at least about 15.5, at least about 16, at least about 16.5, at least about 17, at least about 17.5, at least about 18, at least about 18.5, at least about 19, at least about 19.5 and/or not more than about 45, not more than about 40, not more than about 35, not more than about 33, not more than about 30, not more than about 27, not more than about 25, not more than about 22, not more than about 21.5, not more than about 21, not more than about 20.5, or not more than about 20 weight percent, or in the range of from about 14 to about 45, about 16 to about 30, about 18 to about 25, about 18.5 to about 20, or about 19.5 to about 21 weight percent.

The other poly(vinyl acetal) resin can have a residual hydroxyl content of at least about 8, at least about 9, at least about 10, at least about 11 weight percent and/or not more than about 16, not more than about 15, not more than about 14.5, not more than about 13, not more than about 11.5, not more than about 11, not more than about 10.5, not more than about 10, not more than about 9.5, or not more than about 9 weight percent, or in the range of from about 8 to about 16, about 9 to about 15, or about 9.5 to about 14.5 weight percent, and can be selected such that the difference between the residual hydroxyl content of the first and second poly(vinyl acetal) resin is at least about 2 weight percent, as mentioned previously. One or more other poly(vinyl acetal) resins may also be present in the resin composition, layer, or interlayer and can have a residual hydroxyl within the ranges provided above. Additionally, the residual hydroxyl content of the one or more other poly(vinyl acetal) resins can be the same as or different than the residual hydroxyl content of the first and/or second poly(vinyl acetal) resins.

In some embodiments, at least one of the first and second poly(vinyl acetal) resins can have a residual acetate content different than the other. For example, in some embodiments, the difference between the residual acetate content of the first and second poly(vinyl acetal) resins can be at least about 2, at least about 3, at least about 4, at least about 5, at least about 8, at least about 10 weight percent. One of the poly(vinyl acetal) resins may have a residual acetate content of not more than about 4, not more than about 3, not more than about 2, or not more than about 1 weight percent, measured as described above. In some embodiments, at least one of the first and second poly(vinyl acetal) resins can have a residual acetate content of at least about 5, at least about 8, at least about 10, at least about 12, at least about 14, at least about 16, at least about 18, at least about 20, or at least about 30 weight percent. The difference in the residual acetate content between the first and second poly(vinyl acetal) resins can be within the ranges provided above, or the difference can be less than about 3, not more than about 2, not more than about 1, or not more than about 0.5 weight percent. Additional poly(vinyl acetal) resins present in the resin composition or interlayer can have a residual acetate content the same as or different than the residual acetate content of the first and/or second poly(vinyl acetal) resin.

In some embodiments, the difference between the residual hydroxyl content of the first and second poly(vinyl acetal) resins can be less than about 2, not more than about 1, not more than about 0.5 weight percent and the difference in the residual acetate content between the first and second poly(vinyl acetal) resins can be at least about 3, at least about 5, at least about 8, at least about 15, at least about 20, or at least about 30 weight percent. In other embodiments, the difference in the residual acetate content of the first and second poly(vinyl acetal) resins can be less than about 3, not more than about 2, not more than about 1, or not more than about 0.5 weight percent and the difference in the residual hydroxyl content of the first and second poly(vinyl acetal) resins can be at least about 2, at least about 5, at least about 10, at least about 12, at least about 15, at least about 20, or at least about 30 weight percent.

In various embodiments, the differences in residual hydroxyl and/or residual acetate content of the first and second poly(vinyl acetal) resins can be selected to control or provide certain performance properties, such as strength, impact resistance, penetration resistance, processability, or acoustic performance to the final composition, layer, or interlayer. For example, poly(vinyl acetal) resins having a higher residual hydroxyl content, usually greater than about 16 weight percent, can facilitate high impact resistance, penetration resistance, and strength to a resin composition or layer, while lower hydroxyl content resins, usually having a residual hydroxyl content of less than 16 weight percent, can improve the acoustic performance of the interlayer or blend.

Poly(vinyl acetal) resins having higher or lower residual hydroxyl contents and/or residual acetate contents may also, when combined with at least one plasticizer, ultimately include different amounts of plasticizer. As a result, layers or domains formed of first and second poly(vinyl acetal) resins having different compositions may also have different properties within a single resin layer or interlayer. Although not wishing to be bound by theory, it is assumed that the compatibility of a given plasticizer with a poly(vinyl acetal) resin can depend, at least in part, on the composition of the polymer, and, in particular, on its residual hydroxyl content. Overall, poly(vinyl acetal) resins with higher residual hydroxyl contents tend to exhibit a lower compatibility (or capacity) for a given plasticizer as compared to similar resins having a lower residual hydroxyl content. As a result, poly(vinyl acetal) resins with higher residual hydroxyl contents tend to be less plasticized and exhibit higher stiffness than similar resins having lower residual hydroxyl contents. Conversely, poly(vinyl acetal) resins having lower residual hydroxyl contents may tend to, when plasticized with a given plasticizer, incorporate higher amounts of plasticizer, which may result in a softer resin layer that exhibits a lower glass transition temperature than a similar resin having a higher residual hydroxyl content. Depending on the specific resin and plasticizer, these trends could be reversed.

When two poly(vinyl acetal) resins having different levels of residual hydroxyl content are blended with a plasticizer, the plasticizer may partition between the resin layers or domains, such that more plasticizer can be present in the layer or domain having the lower residual hydroxyl content and less plasticizer may be present in the layer or domain having the higher residual hydroxyl content. Ultimately, a state of equilibrium is achieved between the two resins. The correlation between the residual hydroxyl content of a poly(vinyl acetal) resin and plasticizer compatibility/capacity can facilitate addition of a proper amount of plasticizer to the polymer resin. Such a correlation also helps to stably maintain the difference in plasticizer content between two or more resins when the plasticizer would otherwise migrate between the resins.

In some embodiments, a resin layer or interlayer can include at least a first resin layer comprising a first poly(vinyl acetal) resin and a first plasticizer, and a second resin layer, adjacent to the first resin layer, comprising a second poly(vinyl acetal) resin and a second plasticizer. The first and second plasticizer can be the same type of plasticizer, or the first and second plasticizers may be different. In some embodiments, at least one of the first and second plasticizers may also be a blend of two or more plasticizers, which can be the same as or different than one or more other plasticizers. When one of the first and second poly(vinyl acetal) resins has a residual hydroxyl content that is at least 2 weight percent higher or lower than the residual hydroxyl content of the other, the difference in plasticizer content between the resin layers can be at least about 2, at least about 5, at least about 8, at least about 10, at least about 12, or at least about 15 phr. In most embodiments, the resin layer that includes the resin having a lower hydroxyl content can have the higher plasticizer content. In order to control or retain other properties of the resin layer or interlayer, the difference in plasticizer content between the first and second resin layers may be not more than about 40, not more than about 30, not more than about 25, not more than about 20, or not more than about 17 phr. In other embodiments, the difference in plasticizer content between the first and second resin layers can be at least about 40, at least about 50, at least about 60, or at least about 70 phr.

As a result, in some embodiments, wherein the first and second poly(vinyl acetal) resins are present in adjacent layers of a multilayer interlayer, the first and second resin layers can exhibit different glass transition temperatures. Similarly, when the first and second poly(vinyl acetal) resins are present in a blend, the domains of one of the first and second poly(vinyl acetal) resins can exhibit a different glass transition temperature than the other of the first and second poly(vinyl acetal) resins. Glass transition temperature, or T_(g), is the temperature that marks the transition from the glass state of the polymer to the rubbery state. The glass transition temperatures of the resins and layers described herein were determined by dynamic mechanical thermal analysis (DMTA). The DMTA measures the storage (elastic) modulus (G′) in Pascals, loss (viscous) modulus (G″) in Pascals, and the tan delta (G″/G′) of the specimen as a function of temperature at a given oscillation frequency and temperature sweep rate. The glass transition temperature is then determined by the position of the tan delta peak on the temperature scale. Glass transition temperatures provided herein were determined at an oscillation frequency of 1 Hz under shear mode and a temperature sweep rate of 3° C./min.

The difference in the glass transition temperature of the first resin layer and the second resin layer, or between various regions of a blended resin or resin layer, can be at least about 3, at least about 5, at least about 8, at least about 10, at least about 12, at least about 15, at least about 18, at least about 20, at least about 22, or at least about 25° C. One of the first and second resin layers can have a glass transition temperature of at least about 26, at least about 28, at least about 30, at least about 33, at least about 35° C. and/or not more than about 70, not more than about 65, not more than about 60, not more than about 55, not more than about 50° C., or in the range of from about 26 to about 70, about 30 to about 60, about 35 to about 50° C. The other of the first and second poly(vinyl acetal) resins can have a glass transition temperature of not more than 25, not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 0, not more than about −5, or not more than about −10° C.

When the first and second poly(vinyl acetal) resins are blended with one another such that domains of one resin are dispersed within the other, such differences in plasticizer content and/or glass transition temperature may also exist between domains of the first and second resins. For example, in some embodiments, a resin layer or interlayer may include various domains of higher or lower plasticizer content and/or domains having higher or lower glass transition temperatures, as described previously. In some embodiments, at least a portion of the resin layer or interlayer can have a glass transition temperature of at least about 26, at least about 28, at least about 30, at least about 33, at least about 35° C. and/or not more than about 70, not more than about 65, not more than about 60, not more than about 55, not more than about 50° C., or in the range of from about 26 to about 70, about 28 to about 60, about 35 to about 50° C. and/or at least a portion of the resin layer or interlayer can have a glass transition temperature of not more than 25, not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 0° C., not more than about −5° C., or not more than about −10° C.

One or more resin blends, layers, and interlayers described herein may include various other additives to impart particular properties or features to the interlayer. Such additives can include, but are not limited to, dyes, pigments, stabilizers such as ultraviolet stabilizers, antioxidants, anti-blocking agents, flame retardants, IR absorbers or blockers such as indium tin oxide, antimony tin oxide, lanthanum hexaboride (LaB₆) and cesium tungsten oxide, processing aides, flow enhancing additives, lubricants, impact modifiers, nucleating agents, thermal stabilizers, UV absorbers, dispersants, surfactants, chelating agents, coupling agents, adhesives, primers, reinforcement additives, and fillers.

Additionally, various adhesion control agents (“ACAs”) can be used in the interlayers of the present disclosure to control the adhesion of the sheet to glass. In various embodiments, the amount of ACAs present in a resin composition, layer, or interlayer can be at least about 0.003, at least about 0.01, at least about 0.025 and/or not more than about 0.15, not more than about 0.10, or not more than about 0.04 phr, or in the range of from about 0.003 to about 0.15, about 0.01 to about 0.10, or about 0.025 to about 0.04 phr. Suitable ACAs can include, but are not limited to, sodium acetate, potassium acetate, magnesium bis(2-ethyl butyrate), magnesium bis(2-ethylhexanoate), and combinations thereof, as well as the ACAs disclosed in U.S. Pat. No. 5,728,472.

Resins having different compositions and plasticized resin layers having different properties also tend to exhibit different refractive indices, which can reduce the optical quality of the resulting layer or blend. Although not wishing to be bound by theory, it is believed that such differences in refractive index may cause light that passes through the different resin layers or domains to be refracted in different directions, which may cause haze in the final product. At times, the absolute value of the difference between the refractive index of the first poly(vinyl acetal) resin or layer and the refractive index of the second poly(vinyl acetal) resin or layer, measured according to ASTM D542 at a wavelength of 589 nm and 25° C., can exceed 0.010. As a result, these compositions, layers, or interlayers can have a haze value greater than 5 percent and/or a mottle value greater than 3.

However, in various embodiments of the present invention, compositions, layers, and interlayers comprising a poly(vinyl acetal) resin may further include at least one refractive index (RI) balancing agent for adjusting the refractive index of the composition, layer, or interlayer. In some embodiments, the composition, layer, or interlayer may include at least a first poly(vinyl acetal) resin and a second poly(vinyl acetal) resin along with at least one RI balancing agent. In other embodiments, the composition, layer, or interlayer may include a single poly(vinyl acetal) resin along with at least one RI balancing agent. As discussed above, the RI balancing agent can be any suitable agent present in a resin or a resin blend, layer, or interlayer, or portion thereof, that increases or reduces the refractive index of at least one resin or layer, which may improve the optical properties of the interlayer as compared to an identical interlayer formed without an RI balancing agent. In some embodiments, the resin blend, layer, or interlayer may have a haze value of at least 5 percent when formed in the absence of the RI balancing agent.

The RI balancing agent can be in any suitable form and may be physically blended with one or more resins or it can be chemically bonded, or reacted, with at least one resin so that the RI balancing agent is incorporated into the polymer chain. Examples of RI balancing agents can include, but are not limited to, liquid RI additives, solid RI additives, and residues of at least one aldehyde present in one or more of the poly(vinyl acetal) resins. Various embodiments of RI balancing agents, as well as resin compositions, layers, and interlayers including the same, will now be discussed in detail below.

The RI balancing agent may be present in the resin, resin layer, or interlayer in an amount sufficient to modify the refractive index of poly(vinyl acetal) resin, resin layer, or interlayer. The RI balancing agent may also be present in the composition, layer, or interlayer in an amount sufficient to modify the refractive index of at least one of the two poly(vinyl acetal) resins, thereby minimizing the difference between the refractive indices of two poly(vinyl acetal) resin layers having different refractive indices. The RI balancing agent may also minimize the difference between the refractive index of one or more poly(vinyl acetal) resins and one or more plasticizers within a resin composition, layer, or interlayer. In some embodiments, the RI balancing agent may be present in an amount sufficient to reduce the absolute value of the difference between the refractive index the first poly(vinyl acetal) resin layer and the refractive index of the second poly(vinyl acetal) resin layer to not more than 0.010, not more than about 0.009, not more than about 0.008, not more than about 0.007, not more than about 0.006, not more than about 0.005, not more than about 0.004, or not more than about 0.003. When a multilayer interlayer includes two or more resin layers, the RI balancing agent may be present in one or both layers and can, in some embodiments, be present in one of the layers in a higher amount than in one or more of the other layers.

In some embodiments, the RI balancing agent can comprise one or more residues of an aldehyde having a refractive index of at least 1.421, as measured by ASTM D542 at a wavelength of 589 nm and a temperature of 25° C. The RI balancing aldehyde, which may also be referred to herein as a “high refractive index aldehyde” or “high RI aldehyde,” can have a refractive index of at least about 1.425, at least about 1.450, at least about 1.475, at least about 1.500, at least about 1.510, or at least about 1.515 and/or not more than about 1.675, not more than about 1.650, or not more than about 1.625, or in the range of from about 1.425 to about 1.675, about 1.475 to about 1.650, or about 1.515 to about 1.625. The high RI aldehyde may be an aromatic aldehyde that includes at least one aromatic ring or group. Examples of aromatic aldehydes can include, but are not limited to, C₇ to C₃₀ aromatic aldehydes, C₅ to C₂₅ aromatic aldehydes, or C₉ to C₂₀ aromatic aldehydes. Specific examples of high RI aldehydes that can be used as RI balancing agents in various embodiments of the present invention are listed in Table 1, below.

TABLE 1 Exemplary High RI Aldehydes Aldehyde Refractive Index Hexylcinnamaldehyde 1.517 Benzaldeyde 1.545 Cinnamaldehyde 1.620 4-Chlorobenzaldehyde 1.585 4-t-butylphenylacetaldehyde 1.530 2-phenylpropionaldehyde 1.517 Hydrocinnamaldehyde 1.523

When the RI balancing agent includes residues of at least one high RI aldehyde, at least one of the first and second poly(vinyl acetal) resins can include residues of at least one high RI aldehyde in an amount of at least about 0.5, at least about 1, at least about 5, at least about 10, at least about 15, at least about 20, at least about 25, at least about 30, at least about 35, at least about 40, at least about 45, at least about 50, at least about 55, at least about 60, at least about 65, at least about 70, at least about 75, at least about 80, at least about 85, at least about 90, at least about 95 percent and/or not more than about 99.5, not more than about 99, not more than about 97, not more than about 95, not more than about 90, not more than about 85, not more than about 80, not more than about 75, not more than about 70, not more than about 65, or not more than about 60 weight percent, based on the total weight of aldehyde residues of the first or second poly(vinyl acetal) resin. At least one of the first and second poly(vinyl acetal) resins can include residues of at least one high RI aldehyde in an amount in the range of from about 0.5 to about 99.5, about 10 to about 90, about 25 to about 75, or about 40 to about 60 weight percent, based on the total weight of aldehyde residues of the first or second poly(vinyl acetal) resin.

The amount of high RI aldehyde residues can be determined using a combination of Fourier Transform Infrared Spectroscopy (FT-IR) and Size Exclusion Chromatography (SEC) with UV detection. In particular, FT-IR is used to measure residual hydroxyl content of the resin and SEC is used to determine the amount of high RI aldehyde residues, with the amount of any other aldehyde residues being determined by the difference. The FT-IR analysis is performed using a Perkin Elmer Spectrum 100 FT-IR Spectrometer (commercially available from Perkin Elmer, Waltham, Mass.) with an ATR sampling attachment. The analysis is performed using 8 scans at a 4 cm-1 resolution. Prior to testing, a calibration is generated from several poly(vinyl n-butyral) samples of varying residual hydroxyl content which have been dried in a desiccator with silica overnight at room temperature to remove excess moisture. The peak maximum wave number of the hydroxyl stretching band is correlated with the molar vinyl alcohol content of each sample, which was previously determined by ASTM D1396, and the resulting linear curve fit is used to predict molar residual hydroxyl content the samples being analyzed. These values can be converted to weight percent by calculation after determination of the composition of the poly(vinyl acetal) resin using SEC analysis has been completed, as described below.

The SEC analysis is performed using a Waters 2695 Alliance pump and autosampler with a Waters 410 inline differential refractive index detector and a Waters 2998 PDA inline UV detector (commercially available from Waters Corporation, Milford, Mass.) with Dionex Chromeleon v. 6.8 data acquisition software with an extension pack (commercially available from Thermo Fischer Scientific, Sunnyvale, Calif.). The analysis is performed with a PL Gel Mixed C (5 micron) column and Mixed E (3 micron) columns with an injection volume of 50 microliters at a flow rate of 1.0 mL/minute. Samples are prepared by dissolving between 0.03 and 0.09 grams of resin in 10-15 mL of solvents and then filtering each through a 0.22 micron PTFE filter. Calibrations of the chromatograph are performed using polystyrene standards (commercially available as PSBR250K from American Polymer Standard Corporation, Mentor, Ohio).

In some embodiments, only one of the first and second poly(vinyl acetal) resins includes residues of the high RI aldehyde, while, in other embodiments, both of the resins may include such residues. The refractive index of a resin comprising residues of a high RI aldehyde can be at least about 1.492, at least about 1.495, at least about 1.500, at least about 1.505, at least about 1.510, or at least about 1.515.

In various embodiments, at least one of the first and second poly(vinyl acetal) resins may also include residues of at least one aldehyde having a refractive index of less than 1.421. Examples of these aldehydes can include, for example, aliphatic aldehydes such as the C₄ to C₈ aldehydes discussed above. The aldehydes having a refractive index of less than 1.421 can be selected from the group consisting of n-butyraldehyde, iso-butyraldehyde, and 2-ethylhexyl aldehyde.

When these residues are present, the first and/or second poly(vinyl acetal) resin can include at least about 10, at least about 15, at least about 20, at least about 25, at least about 30, at least about 35, at least about 40, at least about 45, at least about 50, at least about 55, at least about 60, at least about 65, at least about 70, at least about 75, at least about 80, at least about 85, at least about 90, at least about 95 percent and/or not more than about 99, not more than about 97, not more than about 95, not more than about 90, not more than about 85, not more than about 80, not more than about 75, not more than about 70, not more than about 65, or not more than about 60 weight percent, of these aldehydes, based on the total weight of aldehyde residues of the first or second poly(vinyl acetal) resin.

The amount of residues of an aldehyde having a refractive index of less than 1.421 are determined using the FT-IR/SEC method described above and then by calculation according to the following formula: 100 weight percent—weight percent residual hydroxyl (from FT-IR)—weight percent of high RI aldehyde residues (from SEC)—weight percent residual acetate (from FT-IR)=weight percent of residues of aldehyde having refractive index less than 1.421. The first and/or second poly(vinyl acetal) resin can include residues of an aldehyde having a refractive index of less than 1.421 in an amount in the range of from about 10 to about 99, about 25 to about 75, or about 40 to about 60 weight percent, based on the total weight of aldehyde residues of the first or second poly(vinyl acetal) resin. The refractive index of one of these resins can be less than about 1.492, less than about 1.491, or less than about 1.490, measured as described previously.

According to some embodiments, one of the first and second poly(vinyl acetal) resins primarily includes residues of a high RI aldehyde, while the other of the first and second poly(vinyl acetal) resins primarily includes residues of at least one aldehyde having a refractive index of less than 1.421. As used herein, the term “primarily” means at least 75 weight percent, so that a poly(vinyl acetal) resin primarily including residues of a specified aldehyde includes at least 75 weight percent of residues of the specified aldehyde, based on the total weight of aldehyde residues of that resin. The poly(vinyl acetal) resin primarily including residues of a high RI aldehyde can include not more than about 25, not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 2, or not more than about 1 weight percent of residues of other aldehydes having a refractive index less than 1.421, based on the total weight of aldehyde residues of the resin.

Similarly, the other poly(vinyl acetal) resin, which can primarily include residues of an aldehyde having a refractive index of less than 1.421, may comprise not more than about 25, not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 2, or not more than about 1 weight percent of residues of a high RI aldehyde, based on the total weight of aldehyde residues of the resin, and may include at least about 75, at least about 80, at least about 85, at least about 90, at least about 95, at least about 97, or at least about 99 percent of residues of one or more aldehydes having a refractive index less than 1.421. In some embodiments, the ratio of the resin primarily including residues of the high RI aldehyde to the other resin or resins in the composition can be at least about 1:99, at least about 5:95, at least about 10:90, at least about 20:80, at least about 25:75, at least about 30:70, at least about 40:60 and/or not more than about 99:1, not more than about 95:5, not more than about 90:10, not more than about 85:15, not more than about 75:25, not more than about 70:30, or not more than about 60:40, or in the range of from about 1:99 to 99:1, about 10:90 to about 90:10, about 25:75 to 75:25, or about 40:60 to 60:40.

In other embodiments, at least one of the first and second poly(vinyl acetal) resins includes residues of a high RI aldehyde and at least one aldehyde having a refractive index of less than 1.421, thereby forming a “hybrid” resin that includes residues of both high and low RI aldehydes. According to these embodiments, the amounts of the high RI aldehyde residues and the residues of aldehydes having a refractive index of less than 1.421, as well as the weight ratios of one to the other, in the hybrid resin can be within the same ranges provided above with respect to the resin blends. When the first or second poly(vinyl acetal) resin includes residues of both high RI and lower RI aldehydes, the other of the two poly(vinyl acetal) resins may also include residues of at least one high RI aldehyde. Alternatively, the other of the two resins may include little or no high RI aldehyde residues, such that it includes less than about 10, less than about 5, less than about 2, or less than about 1 weight percent of residues of a high RI aldehyde, with the balance being residues of an aldehyde having a refractive index of less than 1.421, including, for example, aldehydes selected from the group consisting of n-butyraldehyde, iso-butyraldehyde, 2-ethylhexyl aldehyde, and combinations thereof.

When the interlayer is a multilayer interlayer, it can include at least one resin layer having at least a first poly(vinyl acetal) resin and another resin layer comprising at least a second poly(vinyl acetal) resin, wherein the difference between the residual hydroxyl content of the first poly(vinyl acetal) resin and the second poly(vinyl acetal) resin is at least 2 weight percent. One or both of the poly(vinyl acetal) resins can include residues of a high RI aldehyde and one of the resin layers may have a refractive index that is higher or lower than the other by at least about 0.002, at least about 0.003, at least about 0.004 and/or not more than about 0.010, not more than about 0.009, not more than about 0.008, or not more than about 0.007, or by an amount in the range of from about 0.002 to about 0.010, about 0.003 to about 0.009, or about 0.004 to about 0.007. In some embodiments when the interlayer includes at least three resin layers, the innermost resin layer can have the higher refractive index, while in other embodiments, the refractive index of one or both of the outer resin layers may be higher. In some embodiments, only one of the first and second poly(vinyl acetal) resins may include residues of the high RI aldehyde. In other embodiments, both of the poly(vinyl acetal) resins may include residues of at least one high RI aldehyde, but the resins can still exhibit a difference in refractive index within the ranges provided above.

One or both of the poly(vinyl acetal) resins can include residues of at least one high RI aldehyde. In some embodiments, when the poly(vinyl acetal) resin including such residues has a residual hydroxyl content of not more than, for example, 15 weight percent, the resin layer including such a resin may have a glass transition temperature of less than 20, not more than about 15, not more than about 10, not more than about 5, not more than about 0, not more than about −5, or not more than about −10° C. and a refractive index of at least about 1.465, at least about 1.470, at least about 1.475, at least about 1.480, at least about 1.485, or at least about 1.490, each measured as described previously. The plasticizer content of the layer, according to various embodiments, can be at least about 50, at least about 55, at least about 60, at least about 65 phr and/or not more than about 120, not more than about 110, not more than about 90, not more than about 85, not more than about 80, or not more than about 75 phr, or in the range of from about 50 to about 120, about 55 to about 110, about 60 to about 90, or about 65 to about 75 phr.

When the resin having the residues of a high RI aldehyde in the multilayer interlayer discussed above has a residual hydroxyl content greater than, for example 16 weight percent, the resin layer including that resin may have a glass transition temperature of at least about 26, at least about 30, at least about 33, or at least about 35° C., and a refractive index of at least about 1.470, at least about 1.475, at least about 1.480, at least about 1.485, or at least about 1.490, each measured as described previously. The plasticizer content of the layer, according to some embodiments, can be less than 50 phr, not more than about 45 phr, not more than about 40 phr, not more than about 30, not more than about 20 phr.

According to various embodiments of the present invention, the RI balancing agent can comprise a liquid RI balancing agent. As used herein, the term “liquid RI balancing agent” refers to an RI balancing agent that is liquid at standard conditions of 25° C. and 1 atm. In some embodiments, the liquid RI balancing agent can be, for example, a high RI plasticizer. As used herein, the term “high RI plasticizer,” refers to a plasticizer having a refractive index of at least 1.460, measured as described previously. The high RI plasticizers suitable for use as RI balancing agents can have a refractive index of at least about 1.460, at least about 1.470, at least about 1.480, at least about 1.490, at least about 1.500, at least about 1.510, at least about 1.520 and/or not more than about 1.600, not more than about 1.575, or not more than about 1.550, measured as discussed above. The refractive index of the high RI plasticizers may be in the range of from about 1.460 to about 1.600, about 1.470 to about 1.575, about 1.480 to about 1.550, about 1.490 to about 1.525, and/or the refractive index of the high RI plasticizers may be at least 1.460, at least 1.650, at least 1.700.

Examples of types or classes of high RI plasticizers can include, but are not limited to, polyadipates (RI of about 1.460 to about 1.485); epoxides such as epoxidized soybean oils (RI of about 1.460 to about 1.480); phthalates and terephthalates (RI of about 1.480 to about 1.540); benzoates and toluates (RI of about 1.480 to about 1.550); and other specialty plasticizers (RI of about 1.490 to about 1.520).

General examples of suitable high RI plasticizers can include, but are not limited to dioctyl terephthalate, dioctyl isophthalate, dioctyl phthalate, octyl benzoate, diisononyl terephthalate, diisononyl isophthalate, diisononyl phthalate, isononyl benzoate, di-2-ethylhexyl terephthalate, di-2-ethylhexyl isophthalate, di-2-ethylhexyl phthalate, 2-ethylhexyl benzoate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethyl) isophthalate, bis-(ethoxyethyl) phthalate, ethoxyethyl benzoate, bis-(ethoxyethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) isophthalate, bis-(ethoxyethoxyethyl) phthalate, ethoxyethoxyethyl benzoate, bis-(butoxyethoxyethyl) terephthalate, bis-(butoxyethoxyethyl) isophthalate, bis-(butoxyethoxyethyl) phthalate, butoxyethoxyethyl benzoate, bis-(butoxyethoxyethoxyethyl) terephthalate, bis-(butoxyethoxyethoxyethyl) isophthalate, bis-(butoxyethoxyethoxyethyl) phthalate, butoxyethoxyethoxyethyl benzoate, bis-(butoxyethyl) terephthalate, bis-(butoxyethyl) isophthalate, bis-(butoxyethyl) phthalate, butoxyethyl benzoate, bis-(methoxyethyl) terephthalate, bis-(methoxyethyl) isophthalate, bis-(methoxyethyl) phthalate, methoxyethyl benzoate, bis-(2-ethylhexyloxyethyl) terephthalate, bis-(2-ethylhexyloxyethyl) isophthalate, bis-(2-ethylhexyloxyethyl) phthalate, 2-ethylhexyloxyethyl benzoate, bis-(2-ethyl hexyloxyethoxyethyl) terephthalate, bis-(2-ethyl hexyloxyethoxyethyl) isophthalate, bis-(2-ethylhexyloxyethoxyethyl) phthalate, 2-ethyl hexyloxyethoxyethyl benzoate, bis-(2-ethyl hexyloxyethoxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethoxyethoxyethyl) isophthalate, bis-(2-ethyl hexyloxyethoxyethoxyethyl) phthalate, 2-ethyl hexyloxyethoxyethoxyethyl benzoate, bis-(dodecyl) terephthalate, bis-(dodecyl) isophthalate, bis-(dodecyl) phthalate, dodecyl benzoate, dipropylene glycol benzoate pelargonate, diethylene glycol benzoate, di-α-propylene glycol benzoate, di-β-propylene glycol benzoate, triethylene glycol benzoate caprylate, triethylene glycol benzoate caprate, diethylene glycol benzoate caprylate, diethylene glycol benzoate caprate, tetraethylene glycol benzoate caprylate, tetraethylene glycol benzoate caprate, 1,4-cyclohexanedimethanol benzoate pelargonate, diethylene glycol benzoate laurate, triethylene glycol benzoate laurate, tetraethylene glycol benzoate laurate, bis-(n-hexyl) terephthalate, bis-(n-hexyl) isophthalate, bis-(n-hexyl) phthalate, n-hexyl benzoate, bis-(n-butyl) terephthalate, bis-(n-butyl) isophthalate, bis-(n-butyl) phthalate, n-butyl benzoate, bis-(iso-octyl) terephthalate, bis-(iso-octyl) isophthalate, bis-(iso-octyl) phthalate, iso-octyl benzoate, 1,2-butanediol dibenzoate, 1,3-butanediol dibenzoate, 1,4-butanediol dibenzoate, di-α-propylene glycol di-o-toluate, tri-α-propylene glycol di-o-toluate, tetra-α-propylene glycol di-o-toluate, di-β-propylene glycol di-o-toluate, tri-β-propylene glycol di-o-toluate, tetra-β-propylene glycol di-o-toluate, diethylene glycol di-o-toluate, triethylene glycol di-o-toluate, tetraethylene glycol di-o-toluate, 2-butyl-2-ethyl-1,3-propanediol dibenzoate, 3-methyl-1,5-pentanediol dibenzoate, diethylene glycol di-p-toluate, triethylene glycol di-p-toluate, tetraethylene glycol di-p-toluate, diethylene glycol di-m-toluate, triethylene glycol di-m-toluate, tetraethylene glycol di-m-toluate, di-α-propylene glycol di-p-toluate, tri-α-propylene glycol di-p-toluate, tetra-α-propylene glycol di-p-toluate, di-β-propylene glycol di-m-toluate, tri-β-propylene glycol di-m-toluate, tetra-β-propylene glycol di-m-toluate, di-α-propylene glycol di-p-toluate, tri-α-propylene glycol di-p-toluate, tetra-α-propylene glycol di-p-toluate, di-β-propylene glycol di-m-toluate, tri-β-propylene glycol di-m-toluate, tetra-β-propylene glycol di-m-toluate, triethylene glycol benzoate acetate, trioctyl trimellitate, and/or combinations thereof.

Specific examples of suitable high RI plasticizers can include, but are not limited to, dipropylene glycol dibenzoate, tripropylene glycol dibenzoate, polypropylene glycol dibenzoate, isodecyl benzoate, 2-ethylhexyl benzoate, diethylene glycol benzoate, butoxyethyl benzoate, butoxyethyoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, propylene glycol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol dibenzoate, 2,2,4-trimethyl-1,3-pentanediol benzoate isobutyrate, 1,3-butanediol dibenzoate, diethylene glycol di-o-toluate, triethylene glycol di-o-toluate, dipropylene glycol di-o-toluate, 1,2-octyl dibenzoate, tri-2-ethylhexyl trimellitate, di-2-ethylhexyl terephthalate, bis-phenol A bis(2-ethylhexaonate), di-(butoxyethyl) terephthalate, di-(butoxyethyoxyethyl) terephthalate, and mixtures thereof. The high RI plasticizer may be selected from dipropylene glycol dibenzoate and tripropylene glycol dibenzoate, and/or 2,2,4-trimethyl-1,3-pentanediol dibenzoate, trioctyl trimellitate, and/or combinations thereof.

In one embodiment, the high RI plasticizer comprises bis-(methoxyethyl) terephthalate, bis-(butoxyethyl) terephthalate, bis-(butoxyethoxyethyl) terephthalate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethyl) terephthalate, bis-(2-ethylhexyl) iso-phthalate, bis-(2-ethylhexyloxyethoxyethyl) terephthalate, 2-ethyl hexyloxyethyl benzoate, 2-ethyl hexyloxyethoxylethyl benzoate, ethoxyethoxyethyl benzoate, butoxyethoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, dodecyl benzoate, dipropylene glycol di-o-toluate, triethylene glycol benzoate acetate, trioctyl trimellitate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises bis-(methoxyethyl) terephthalate, bis-(butoxyethyl) terephthalate, bis-(butoxyethoxyethyl) terephthalate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(2-ethyl hexyloxyethoxyethyl) terephthalate, 2-ethyl hexyloxyethoxylethyl benzoate, ethoxyethoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, dipropylene glycol di-o-toluate and triethylene glycol benzoate acetate, trioctyl trimellitate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises bis-(methoxyethyl) terephthalate, bis-(butoxyethyl) terephthalate, bis-(butoxyethoxyethyl) terephthalate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, ethoxyethoxyethyl benzoate, dipropylene glycol di-o-toluate, and triethylene glycol benzoate acetate, trioctyl trimellitate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises dioctyl phthalate, diisononyl phthalate, di-2-ethylhexyl terephthalate, bis-(methoxyethyl) terephthalate, bis-(butoxyethyl) terephthalate, bis-(butoxyethoxyethyl) terephthalate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethyl) terephthalate, bis-(2-ethylhexyl) iso-phthalate, bis-(2-ethylhexyloxyethoxyethyl) terephthalate, 2-ethyl hexyloxyethyl benzoate, 2-ethyl hexyloxyethoxylethyl benzoate, ethoxyethoxyethyl benzoate, butoxyethoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, dodecyl benzoate, dipropylene glycol di-o-toluate, triethylene glycol benzoate acetate, trioctyl trimellitate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises bis-(methoxyethyl) terephthalate, bis-(butoxyethyl) terephthalate, bis-(butoxyethoxyethyl) terephthalate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethyl) terephthalate, bis-(2-ethylhexyl) iso-phthalate, ethoxyethoxyethyl benzoate, butoxyethoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, dodecyl benzoate, dipropylene glycol di-o-toluate, triethylene glycol benzoate acetate, trioctyl trimellitate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises bis-(butoxyethyl) terephthalate, bis-(butoxyethoxyethyl) terephthalate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(2-ethylhexyl) iso-phthalate, butoxyethoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, dodecyl benzoate, dipropylene glycol di-o-toluate, triethylene glycol benzoate acetate, trioctyl trimellitate, or combinations thereof.

In another embodiment, the plasticizer comprises a terephthalate comprising one of the following compounds: dioctyl terephthalate, diisononyl terephthalate, bis-(2-ethylhexyloxyethyl) terephthalate, bis-(2-ethylhexyl) terephthalate, bis-(2-ethylhexyloxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethoxyethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(dodecyl) terephthalate, bis-(n-hexyl) terephthalate, bis-(n-butyl) terephthalate, bis-(iso-octyl) terephthalate, bis-(ethoxyethyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(butoxyethoxyethyl) terephthalate, bis-(butoxyethoxyethoxyethyl) terephthalate, bis-(butoxyethyl) terephthalate, bis-(methoxyethyl) terephthalate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises an isophthalate comprising one of the following compounds: dioctyl isophthalate, diisononyl isophthalate, di-2-ethylhexyl isophthalate, bis-(ethoxyethyl) isophthalate, bis-(ethoxyethoxyethyl) isophthalate, bis-(butoxyethoxyethyl) isophthalate, bis-(butoxyethoxyethoxyethyl) isophthalate, bis-(butoxyethyl) isophthalate, bis-(methoxyethyl) isophthalate, bis-(2-ethylhexyloxyethyl) isophthalate, bis-(2-ethylhexyloxyethoxyethyl) isophthalate, bis-(2-ethylhexyloxyethoxyethoxyethyl) isophthalate, bis-(ethoxyethoxyethyl) isophthalate, bis-(dodecyl) isophthalate, bis-(n-hexyl) isophthalate, bis-(n-butyl) isophthalate, bis-(iso-octyl) isophthalate, bis-(2-ethylhexyl) isophthalate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises a phthalate comprising one of the following compounds: dioctyl phthalate, diisononyl phthalate, bis-(ethoxyethyl) phthalate, bis-(ethoxyethoxyethyl) phthalate, bis-(butoxyethoxyethyl) phthalate, bis-(butoxyethoxyethoxyethyl) phthalate, bis-(butoxyethyl) phthalate, bis-(methoxyethyl) phthalate, bis-(2-ethylhexyloxyethyl) phthalate, bis-(2-ethylhexyl) phthalate, bis-(2-ethylhexyloxyethoxyethyl) phthalate, bis-(2-ethyl hexyloxyethoxyethoxyethyl) phthalate, bis-(ethoxyethoxyethyl) phthalate, bis-(dodecyl) phthalate, bis-(n-hexyl) phthalate, bis-(n-butyl) phthalate, bis-(iso-octyl) phthalate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises a benzoate comprising one of the following compounds: octyl benzoate, isononyl benzoate, ethoxyethoxyethyl benzoate, butoxyethyl benzoate, methoxyethyl benzoate, 2-ethylhexyl benzoate, 2-ethylhexyloxyethoxyethoxyethyl benzoate, ethoxyethoxyethyl benzoate, diethylene glycol benzoate, di-α-propylene glycol benzoate, di-β-propylene glycol benzoate, n-hexyl benzoate, n-butyl benzoate, iso-octyl benzoate, ethoxyethyl benzoate, butoxyethoxyethyl benzoate, butoxyethoxyethoxyethyl benzoate, or combinations thereof

In another embodiment, the high RI plasticizer comprises a toluate comprising one of the following compounds: di-α-propylene glycol di-o-toluate, tri-α-propylene glycol di-o-toluate, tetra-α-propylene glycol di-o-toluate, di-β-propylene glycol di-o-toluate, tri-β-propylene glycol di-o-toluate, tetra-β-propylene glycol di-o-toluate, triethylene glycol di-o-toluate, tetraethylene glycol di-o-toluate, diethylene glycol di-p-toluate, tetraethylene glycol di-p-toluate, diethylene glycol di-m-toluate, triethylene glycol di-m-toluate, tetraethylene glycol di-m-toluate, di-α-propylene glycol di-p-toluate, tri-α-propylene glycol di-p-toluate, tetra-α-propylene glycol di-p-toluate, di-β-propylene glycol di-m-toluate, tri-β-propylene glycol di-m-toluate, tetra-β-propylene glycol di-m-toluate, di-α-propylene glycol di-p-toluate, tri-α-propylene glycol di-p-toluate, tetra-α-propylene glycol di-p-toluate, di-β-propylene glycol di-m-toluate, tri-β-propylene glycol di-m-toluate, tetra-β-propylene glycol di-m-toluate, diethylene glycol di-o-toluate, triethylene glycol di-p-toluate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises a mixed benzoate comprising one of the following compounds: dipropylene glycol benzoate pelargonate, triethylene glycol benzoate caprylate, triethylene glycol benzoate caprate, diethylene glycol benzoate caprylate, diethylene glycol benzoate caprate, tetraethylene glycol benzoate caprylate, tetraethylene glycol benzoate caprate, 1,4-cyclohexanedimethanol benzoate pelargonate, diethylene glycol benzoate laurate, triethylene glycol benzoate laurate, tetraethylene glycol benzoate laurate, triethylene glycol benzoate acetate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises at least one of following: (i) a terephthalate comprising one of the following compounds: bis-(2-ethylhexyloxyethoxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethyl) terephthalate, bis-(dodecyl) terephthalate, bis-(ethoxyethoxyethyl) terephthalate, bis-(ethoxyethoxyethoxyethyl) terephthalate, bis-(butoxyethoxyethoxyethyl) terephthalate, or combinations thereof; (ii) an isophthalate comprising one of the following compounds: bis-(2-ethylhexyloxyethoxyethoxyethyl) isophthalate, bis-(2-ethylhexyloxyethoxyethyl) isophthalate, bis-(2-ethylhexyloxyethyl) isophthalate, bis-(butoxyethoxyethyl) isophthalate, bis-(butoxyethyl) isophthalate, bis-(dodecyl) isophthalate, bis-(ethoxyethoxyethyl) isophthalate. bis-(ethoxyethoxyethyl) isophthalate, bis-(ethoxyethyl) isophthalate, bis-(2-ethylhexyloxyethoxyethoxyethyl) isophthalate, bis-(ethoxyethoxyethoxyethyl) isophthalate, bis-(butoxyethoxyethoxyethyl) isophthalate, or combinations thereof; (iii) a phthalate comprising one of the following compounds: bis-(2-ethyl hexyloxyethoxyethoxyethyl) phthalate, bis-(2-ethyl hexyloxyethoxyethyl) phthalate, bis-(2-ethylhexyloxyethyl) phthalate, bis-(2-ethylhexyloxyethoxyethoxyethyl) phthalate, bis-(ethoxyethoxyethoxyethyl) phthalate, bis-(butoxyethoxyethoxyethyl) phthalate, or combinations thereof; (iv) a benzoate comprising the following compound: 2-ethylhexyloxyethoxyethoxyethyl benzoate; (v) a toluate comprising one of the following compounds: diethylene glycol di-m-toluate, diethylene glycol di-p-toluate, di-α-propylene glycol di-o-toluate, di-α-propylene glycol di-p-toluate, di-α-propylene glycol di-p-toluate, di-β-propylene glycol di-m-toluate, di-β-propylene glycol di-m-toluate, di-β-propylene glycol di-o-toluate, tetraethylene glycol di-m-toluate, tetraethylene glycol di-o-toluate, tetraethylene glycol di-p-toluate, tetra-α-propylene glycol di-o-toluate, tetra-α-propylene glycol di-p-toluate, tetra-α-propylene glycol di-p-toluate, tetra-β-propylene glycol di-m-toluate, tetra-β-propylene glycol di-m-toluate, tetra-β-propylene glycol di-o-toluate, triethylene glycol di-m-toluate, triethylene glycol di-o-toluate, tri-α-propylene glycol di-o-toluate, tri-α-propylene glycol di-p-toluate, tri-α-propylene glycol di-p-toluate, tri-β-propylene glycol di-m-toluate, tri-β-propylene glycol di-m-toluate, tri-β-propylene glycol di-o-toluate, or combinations thereof; and/or (vi) a mixed benzoate comprising one of the following compounds: 1,4-cyclohexanedimethanol dibenzoate, 1,4-cyclohexanedimethanol benzoate pelargonate, 1,4-cyclohexanedimethanol benzoate laurate, 1,4-cyclohexanedimethanol benzoate caprate, 1,4-cyclohexanedimethanol benzoate caprylate, 3-methyl-1,5-pentanediol dibenzoate, diethyleneglycol benzoate caprate, diethyleneglycol benzoate caprylate, diethyleneglycol benzoate laurate, dipropyleneglycol benzoate pelargonate, tetraethyleneglycol benzoate caprate, tetraethyleneglycol benzoate caprylate, tetraethyleneglycol benzoate laurate, triethyleneglycol benzoate laurate, or combinations thereof.

In another embodiment, the high RI plasticizer comprises at least one of following compounds:

or a combination thereof; wherein R is selected from the group consisting of hydrogen and a methyl group; wherein R′ is selected from the group consisting of hydrogen and an alkyl group having from 1 to 12 carbon atoms; and wherein n is at least 3.

In another embodiment, R is a hydrogen, R is a methyl group, R is an ethyl group, R is a propyl group, and/or R is an alkyl group having 1 to 5 carbon atoms. In another embodiment, R′ comprises a methyl, ethyl, propyl, n-butyl, sec-butyl, pentyl, n-hexyl, 2-ethyl hexyl, heptyl, octyl group, or a combination therein. In another embodiment, n is at least 3, n is at least 4, n is at least 5, n is at least 7, n is at least 3 but less than 10, n is at least 3 but less than 9, n is at least 3 but less than 8, n is at least 3 but less than 7, n is at least 3 but less than 6, n is at least 3 but less than 5, n is at least 4 but less than 10, n is at least 4 but less than 9, n is at least 4 but less than 8, n is at least 4 but less than 7, and/or n is at least 4 but less than 6.

In another embodiment, the high RI plasticizer comprises at least one of the following compounds: bis-(2-ethylhexyloxyethoxyethoxyethyl) terephthalate, bis-(ethoxyethoxyethoxyethyl) terephthalate, bis-(butoxyethoxyethoxyethyl) terephthalate, bis-(2-ethylhexyloxyethoxyethoxyethyl) isophthalate, bis-(ethoxyethoxyethoxyethyl) isophthalate, bis-(butoxyethoxyethoxyethyl) isophthalate, bis-(2-ethylhexyloxyethoxyethoxyethyl) phthalate, bis-(ethoxyethoxyethoxyethyl) phthalate, bis-(butoxyethoxyethoxyethyl) phthalate, or combinations thereof.

When the resin layer or interlayer includes a high RI plasticizer, the plasticizer can be present in the layer alone or it can be blended with one or more additional plasticizers. The other plasticizer or plasticizers may also comprise high RI plasticizers, or one or more may be a lower RI plasticizer having a refractive index of less than 1.460. In some embodiments, the lower RI plasticizer may have a refractive index of less than about 1.450, less than about 1.445, or less than about 1.442 and can be selected from the group listed previously. When a mixture of two or more plasticizers are employed as a RI balancing agent, the mixture can have a refractive index within one or more of the above ranges.

When used as an RI balancing agent in a multilayer interlayer, a high RI plasticizer may be present in different amounts in two or more of the resin layers. Similarly, when used as an RI balancing agent in a resin composition or blended resin layer, the high RI plasticizer may be partitioned as described previously, such that resin layers or domains having a lower residual hydroxyl content may have higher amounts of the high RI plasticizer. In some embodiments, at least one layer or portion of a resin layer or interlayer may comprise a high RI plasticizer as an RI balancing agent in an amount of at least about 5, at least about 10, at least about 15, at least about 20, at least about 25, at least about 30, at least about 35 and/or not more than about 50, not more than about 45, or not more than about 40 phr. The high RI plasticizer can be present in the resin layer or interlayer in an amount in the range of from about 5 to about 50, about 10 to about 45, about 20 to about 40 phr. In some embodiments, one or more other layers or portions can include the high RI plasticizer in an amount of at least about 50, at least about 55, at least about 60, at least about 65, at least about 70 and/or not more than about 120, not more than about 110, not more than about 100, not more than about 90, or not more than about 75 phr, or in the range of from about 50 to about 120, about 55 to about 110, about 60 to about 90, about 65 to about 75 phr. These amounts may include any other plasticizers present in the composition, including those having a refractive index less than 1.460, or may include only the high RI plasticizer.

When a high RI plasticizer is used as an RI balancing agent in a multilayer interlayer, the interlayer can include at least one resin layer having a first poly(vinyl acetal) resin and another resin layer comprising a second poly(vinyl acetal) resin, wherein the difference between the residual hydroxyl content of the first poly(vinyl acetal) resin and the second poly(vinyl acetal) resin is at least 2 weight percent. At least one of the resin layers can include a high RI plasticizer in an amount sufficient so that the absolute value of the difference between the refractive index of the resin layer and the refractive index of the another resin layer is not more than 0.010. In some embodiments when the interlayer includes at least three resin layers, the innermost resin layer can have a higher refractive index, while in other embodiments, the refractive index of one or both of the outer resin layers may be higher.

In another embodiment, a high RI plasticizer can be used as an RI balancing agent in a multilayer interlayer, the interlayer can include at least one resin layer having a first poly(vinyl acetal) resin and another resin layer comprising a second poly(vinyl acetal) resin, wherein the difference between the residual hydroxyl content of the first poly(vinyl acetal) resin and the second poly(vinyl acetal) resin is at least 2 weight percent or at least 1 weight percent. At least one of the resin layers can include a high RI plasticizer in an amount sufficient so that the absolute value of the difference between the refractive index of the resin layer and the refractive index of the another resin layer is not more than 0.010. In some embodiments, the interlayer can include at least one resin layer having a first poly(vinyl acetal) resin and a first high RI plasticizer and another resin layer comprising a second poly(vinyl acetal) resin and a second high RI plasticizer, wherein the first high RI plasticizer and the second high RI plasticizer may be the same or different plasticizers. In some embodiments, the first poly(vinyl acetal) resin and a second poly(vinyl acetal) resin may have the same residual hydroxyl content but may vary in their molecular weight and/or residual acetate content. In some embodiments when the interlayer includes at least three resin layers, the innermost resin layer can have a higher refractive index, while in other embodiments, the refractive index of one or both of the outer resin layers may be higher.

When a high RI plasticizer is included in a resin layer that includes at least one poly(vinyl acetal) resin having the lower residual hydroxyl content, at least a portion of the resin layer can have a glass transition temperature of not more than 25, not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 0, not more than about −5, or not more than about −10° C., and the layer can have a refractive index of at least about 1.465, at least about 1.470, at least about 1.475, at least about 1.480, at least about 1.485, or at least about 1.490, at least about 1.495 measured as described previously. The plasticizer content of this layer, in some embodiments, can be at least about 50, at least about 55, at least about 60 phr and/or not more than about 120, not more than about 110, not more than about 90, not more than about 85, not more than about 80, or not more than about 75 phr, or in the range of from about 50 to about 120, about 55 to about 110, about 60 to about 90, or about 60 to about 75 phr.

When the high RI plasticizer is present in the resin layer that comprises the poly(vinyl acetal) resin having a higher residual hydroxyl content, at least a portion of the layer can have a glass transition temperature of at least about 26, at least about 30, at least about 33, or at least about 35° C., and the layer can have a refractive index of at least about 1.470, at least about 1.475, at least about 1.480, at least about 1.485, or at least about 1.490, measured as described previously. The plasticizer content of this layer, according to some embodiments, can be less than 50 phr, not more than about 45 phr, not more than about 40 phr, not more than about 30, or not more than about 20 phr.

According to various embodiments of the present invention, the RI balancing agent may be a solid RI additive present in one or more layers or portions of a layer or interlayer. As used herein, the term “solid RI additive” refers to an additive used to adjust the refractive index of a poly(vinyl acetal) resin, resin layer, or interlayer and which is solid at ambient conditions of 25° C. and 1 atm. In various embodiments, the solid RI additive may have a melting point of at least about 27, at least about 30, at least about 35, at least about 40, at least about 45, at least about 50, at least about 55, at least about 60, at least about 75, at least about 80, at least about 85, at least about 90, at least about 95, or at least about 100° C. When employed in a resin blend, layer, or interlayer, the solid RI additive can be present in an amount sufficient such that the absolute value of the difference between the refractive indices of the first and second resin layers is not more than about 0.010. The difference between the refractive index of the first and second resin layers may be greater than 0.010, when formulated into identical resin layers in the absence of the solid RI additive.

In some embodiments, the solid RI additive can be a high RI solid additive for increasing the refractive index of at least one resin layer or interlayer. The refractive index of the high RI solid additive can be at least about 1.460, at least about 1.465, at least about 1.470, at least about 1.475, at least about 1.480, at least about 1.485, at least about 1.490, at least about 1.495, at least about 1.500, at least about 1.505, at least about 1.510, at least about 1.525, at least about 1.550, at least about 1.575, or at least about 1.600, measured as described previously. In other embodiments, the solid RI additive may be a RI lowering solid additive for reducing the refractive index of at least one resin or resin layer. The RI lowering solid additive can have a refractive index of less than 1.460, not more than about 1.455, not more than about 1.450, not more than about 1.445, or not more than about 1.440, measured as described previously. Whether higher or lower, the solid RI additive can have a refractive index that is at least about 0.005, at least about 0.010, at least about 0.050, at least about 0.10 and/or not more than about 0.50, not more than about 0.35, or not more than about 0.20 different than the refractive index of the poly(vinyl acetal) resin. The difference in refractive index between the solid RI additive and the poly(vinyl acetal) resin can be in the range of from about 0.005 to about 0.50, about 0.010 to about 0.35, or about 0.050 to about 0.35.

In various embodiments, the solid RI additive can be present in a resin composition or interlayer in an amount of at least about 0.5, at least about 1, at least about 1.5, at least about 2, or at least about 5 phr, depending on the specific type of additive and layer or interlayer. The solid RI additive, whether a high RI additive or an RI lowering additive, may comprise a physical solid RI additive capable of being physically mixed or blended with at least one poly(vinyl acetal) resin in a resin composition or layer, or it can be a reactive solid RI additive, which may react with and become incorporated into the backbone of one or more poly(vinyl acetal) resins.

The solid RI additive can be used in combination with one or more low RI plasticizers. Examples of low RI plasticizers can include, but are not limited to, triethylene glycol di-(2-ethylhexanoate) (“3GEH”), triethylene glycol di-(2-ethylbutyrate), triethylene glycol diheptanoate, tetraethylene glycol diheptanoate, tetraethylene glycol di-(2-ethylhexanoate) (“4GEH”), dihexyl adipate, dioctyl adipate, hexyl cyclohexyladipate, diisononyl adipate, heptylnonyl adipate, di(butoxyethyl) adipate, and bis(2-(2-butoxyethoxy)ethyl) adipate, dibutyl sebacate, dioctyl sebacate, and mixtures thereof. The plasticizer may be selected from the group consisting of triethylene glycol di-(2-ethylhexanoate) and tetraethylene glycol di-(2-ethylhexanoate), or the plasticizer can comprise triethylene glycol di-(2-ethylhexanoate). The solid RI additive can also be used in combination with one or more high RI plasticizers mentioned previously.

When the solid RI additive is a physical solid RI additive, it may be combined with one or more poly(vinyl acetal) resins or layers in an interlayer. In some embodiments, the physical solid RI additive may be present in at least one layer or in an interlayer in an amount of at least about 1, at least about 2, at least about 3, at least about 5, at least about 8, at least about 10, at least about 12, at least about 15, at least about 20 and/or not more than about 60, not more than about 55, not more than about 50, not more than about 45, not more than about 40, not more than about 35, not more than about 30, not more than about 25, not more than about 20, or not more than about 15 phr, or in an amount in the range of from about 1 to about 60, about 5 to about 50, or about 10 to about 45 phr. Examples of suitable physical solid high RI additives can include, but are not limited to, polyadipates, polystyrene having a molecular weight of less than 2500, epoxides, phthalic acid esters, benzoic acid esters, inorganic oxides such as, for example, zirconium oxide, and combinations thereof. Physical solid RI lowering additives can be selected from the group consisting of halogenated additives, and silicon-containing additives.

When utilized in a multilayer interlayer, the physical solid RI additive may be present in one of the resin layers in a higher amount than one or more other layers. The difference between the amount of the physical solid RI additive present in one of the resin layers and the amount of physical solid RI additive present in another layer, including, for example, an adjacent layer, can be at least about 2, at least about 5, at least about 8, at least about 10 phr and/or not more than about 30, not more than about 25, or not more than about 20 phr, or it can be in the range of from about 2 to about 30, about 5 to about 25, or about 10 to about 20 phr. According to some embodiments, at least one of the layers can include at least about 1, at least about 5, at least about 10, at least about 15 phr and/or not more than about 60, not more than about 55, not more than about 50, not more than about 45 phr of the physical solid RI additive, or the physical solid RI additive can be present in an amount in the range of from about 1 to about 60, about 10 to about 50, or about 15 to about 45 phr. In some embodiments, the physical solid RI additive can be present in one or more layers in an amount of at least about 5, at least about 10, at least about 15, at least about 20 phr and/or not more than about 60, not more than about 55, not more than about 50 phr, or in an amount in the range of from about 5 to about 60, about 15 to about 55, or about 20 to about 50 phr.

When the multilayer interlayer comprises three or more resin layers and the solid RI additive is a solid high RI additive, the inner, or core, layer or layers can include higher amounts of the physical solid RI additive than the outer, or skin, layers. However, if the solid RI additive is a solid RI lowering additive, the outer skin layers may include higher amounts of the solid RI additive than the inner core layer. The core layer can include at least about 30, at least about 40, at least about 50, at least about 60, at least about 70, or at least about 80 percent of the total amount of physical solid RI additive present in the interlayer.

When the solid RI additive is a reactive solid RI additive, it may be reacted with at least one poly(vinyl acetal) resin such that at least a portion of the additive is incorporated into the polymer chain. The reactive RI additive can be an aromatic additive and can comprise, in some embodiments, phthalic anhydrides and phenylalkoxysilanes including, for example, diphenyldimethoxysilane.

In some embodiments, the reactive RI additive may be present in one layer of a multilayer interlayer in a higher amount than it is present in one or more other layers of the interlayer. In some embodiments, it may be absent, or substantially absent, from one or more resin layers. For example, when the interlayer is a multilayer interlayer including at least three resin layers, the inner core layer may include at least about 0.5, at least about 1, at least about 1.5, at least about 2, at least about 2.5, at least about 3 and/or not more than about 50, not more than about 30, not more than about 20, not more than about 15, not more than about 12, not more than about 10, or not more than about 8 phr of one or more reactive solid RI additives, or an amount in the range of from about 0.5 to about 20, about 1 to about 12, or about 2 to about 8 phr. The outer skin layer or layers may include not more than about 10, not more than about 5, not more than about 2, not more than about 1, or not more than about 0.5 phr of the reactive solid RI additive. The core layer can include at least about 65, at least about 75, at least about 85, at least about 95, or at least about 99 percent of the total amount of the reactive RI additive present in the interlayer.

When a solid RI additive is used as an RI balancing agent in a multilayer interlayer, the interlayer can include at least one resin layer having a first poly(vinyl acetal) resin and another resin layer comprising a second poly(vinyl acetal) resin, wherein the difference between the residual hydroxyl content of the first poly(vinyl acetal) resin and the second poly(vinyl acetal) resin is at least 2 weight percent. At least one of the resin layers can include the high RI additive in an amount sufficient so that the absolute value of the difference between the refractive index of the first resin layer and the refractive index of the second resin layer is not more than 0.010. In some embodiments when the interlayer includes at least three resin layers, the innermost resin layer can have a higher refractive index, while in other embodiments, the refractive index of one or both of the outer resin layers may be higher.

When a solid RI additive is included in a resin layer comprising the poly(vinyl acetal) resin having the lower residual hydroxyl content, the resin layer can have a glass transition temperature of not more than 25, not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 0, not more than about −5, or not more than about −10° C., and a refractive index of at least about 1.465, at least about 1.470, at least about 1.475, at least about 1.480, at least about 1.485, at least about 1.495, or at least about 1.500, each measured as described previously. The plasticizer content of this layer, in some embodiments, can be at least about 50, at least about 55, at least about 60, at least about 65 phr and/or not more than about 120, not more than about 110, not more than about 90, not more than about 85, not more than about 80, or not more than about 75 phr, or in the range of from about 50 to about 120, about 55 to about 110, about 60 to about 90, about 65 to about 75 phr.

When the solid RI additive is present in the resin layer that comprises the poly(vinyl acetal) resin having a higher residual hydroxyl content, the layer can have a glass transition temperature of at least about 26, at least about 30, at least about 33, or at least about 35° C. In some embodiments, the layer can have a refractive index of at least about 1.470, at least about 1.475, at least about 1.480, at least about 1.485, at least about 1.490, at least about 1.500, at least about 1.510. The plasticizer content of this layer, according to some embodiments, can be less than 50 phr, not more than about 45 phr, not more than about 40 phr, not more than about 30, or not more than about 20 phr.

Resin compositions, layers, and interlayers formulated according to various embodiments of the present invention to include at least two poly(vinyl acetal) resins and an RI balancing agent can exhibit enhanced optical properties without sacrificing other properties such as impact resistance and acoustic performance. As discussed above, due to differences in properties or composition of the resins, such as, for example, residual hydroxyl content, residual acetate content, or aldehyde residues, identical blends of the same resins formulated without the RI balancing agent may provide compositions, layers, and interlayers with reduced optical performance.

Clarity is one parameter used to describe the optical performance of compositions, layers, and interlayers described herein and may be determined by measuring haze value or percent. Haze value represents the quantification of light scattered by a sample in contrast to the incident light. In some embodiments, the resin blends, layers, and interlayers described herein may have a haze value of less than 5 percent, less than about 4 percent, less than about 3 percent, less than about 2 percent, less than about 1, or less than about 0.5 percent, as measured in accordance with ASTM D1003-13—Procedure B using Illuminant C, at an observer angle of 2 degrees. The test is performed with a spectrophotometer, such as a Hunterlab UltraScan XE instrument (commercially available from Hunter Associates, Reston, Va.), on a polymer sample having a thickness of 0.76 mm, which has been laminated between two sheets of clear glass each having a thickness of 2.3 mm (commercially available from Pittsburgh Glass Works of Pennsylvania).

In some embodiments, haze value is very low, e.g., less than 5 percent, less than about 4 percent, less than about 3 percent, less than about 2 percent, less than about 1, or less than about 0.5 percent, however, when a bright light is shone on the laminates from behind, an optical defect appearing as a “milky haze,” can be seen when the laminates are viewed at wide angles (>30°). The presence or absence of such a “milky haze” is characterized herein by the HLD haze value. HLD haze is measured by a HLD haze measurement apparatus, which is constructed with a tungsten halogen light source, a sample holder, a goniometer with a light detector mounted on. The HLD haze measurement apparatus is calibrated using a set of HLD standard laminates having a total thickness of 8.3 mm (5 layers of 0.76 mm interlayer) between two 2.3-mm clear glass sheets representing HLD Haze grades 0, 1, 2, and the like, with increasing values indicating increased HLD haze. In this measurement, laminate was made with clear glass having thickness of about 2.3 mm by normal autoclave lamination process. After the autoclave, the laminate was placed at room temperature overnight. The scattered light intensity at a scatted angle of 45° is collected from a testing laminate sample at room temperature using the HLD haze measurement apparatus, and HLD haze is calculated using computer software and reported at a nominal total laminate thickness.

Additionally, the resin layers and interlayers described herein may have a mottle value of not more than 3, not more than 2, or not more than 1. Mottle is another measure of optical quality, which is detected as a texture or graininess. Mottle is a visual defect if the level is too high or too severe, thereby causing objectionable visual appearance. Mottle is assessed and categorized by a side-by-side qualitative comparison of shadowgraph projections for a test laminate with a set of standard laminate shadowgraphs that represent a series, or scale, of mottle values ranging from 1 to 4, with 1 representing a standard of low mottle (i.e., a low number of disruptions) and 4 representing a standard of high mottle (i.e., a high number of disruptions). High mottle is generally considered objectionable, particularly in automotive and architectural applications. Optionally, a model laminate having a single layer interlayer with zero mottle (no mottle) is used to facilitate the evaluation in a test laminate that has a mottle rating lower than the scale of the standard set, such as lower than a rating of 1. A test laminate that shows a shadowgraph projection similar to that of a zero-mottle laminate is assessed to have a mottle rating of zero. The test laminate is prepared with two sheets of clear glass each having a thickness of 2.3 mm (commercially available from Pittsburgh Glass Works of Pennsylvania) and an interlayer. The interlayer typically has a random rough surface R_(z) of about 35 to 40 microns and thickness of 0.76 to 0.86 mm.

The mottle values provided herein were determined using a Clear Mottle Analyzer (CMA) that includes a xenon arc lamp, a sample holder, a projection screen, and a digital camera. The xenon arc lamp is used to project a shadowgraph of a laminated sample onto the screen and the camera is configured to capture an image of the resulting shadowgraph. The image is then digitally analyzed using computer imaging software and compared to images of previously-captured standard samples to determine the mottle of the sample. A method of measuring mottle using a CMA is described in detail in U.S. Patent Application Publication No. US 2012-0133764.

Another parameter used to determine the optical performance is transparency, or percent visual transmittance (% T_(vis)), which is measured using a spectrophotometer, such as a HunterLab UltraScan EX, in accordance with ASTM D1003, Procedure B using Illuminant Cat an observer angle of 2°. The values provided herein were obtained by analyzing a glass laminate samples having an interlayer thickness of about 0.76 mm and a clear glass thickness of 2.3 mm (commercially available from Pittsburgh Glass Works of Pennsylvania). In some embodiments, the resin layers and interlayers of the present invention can have a percent visual transmittance of at least about 70, at least about 75, at least about 80, at least about 81, at least about 82, at least about 83, at least about 84, at least about 85, at least about 85.5, at least about 86, at least about 86.5, at least about 87, at least about 87.5, at least about 88, or at least about 88.5 percent. More specifically, the resin layers and interlayers of the present invention have a % T_(vis) of greater than 85 for the interlayers containing only additives of ACAs, UV stabilizers, and antioxidant, or greater than 80% for the interlayers containing additional additives such as pigments, IR absorbers or blockers as mentioned above. Polymer interlayers containing high levels of pigments and/or dyes may have lower % T_(vis) values as desired, such as in mass pigmented or colored polymer interlayers.

In addition to exhibiting one or more optical properties within the ranges above, the resin layers and interlayers described herein may also exhibit acoustic properties within a desirable range. In some embodiments, as discussed above, at least a portion of a resin layer or interlayer may have a glass transition temperature of not more than 25, not more than about 20, not more than about 15, not more than about 10, not more than about 5, not more than about 0, not more than about −5, or not more than about −10° C., which may facilitate acoustic performance of the layer or interlayer. At the same time, at least a portion of the layer or interlayer may have a glass transition temperature of at least about 26, at least about 30, at least about 35° C., which may facilitate impact resistance properties and strength.

In some embodiments, a resin layer or interlayer according to the present invention may have a tan delta value of at least about 0.70. Tan delta is the ratio of the loss modulus (G″) in Pascals to the storage modulus (G′) in Pascals of a specimen measured by Dynamic Mechanical Thermal Analysis (DMTA). The DMTA is performed with an oscillation frequency of 1 Hz under shear mode and a temperature sweep rate of 3° C./min. The peak value of the G″/G′ curve at the glass transition temperature is the tan delta value. Resin layers or interlayers as described according to various embodiment herein can have a tan delta of at least about 1.0, at least about 1.05, at least about 1.10, at least about 1.25, at least about 1.50, at least about 1.75, at least about 2.0, or at least about 2.25.

Additionally, the resin layers and interlayers can have a damping loss factor, or loss factor, of at least about 0.10, at least about 0.15, at least about 0.17, at least about 0.20, at least about 0.25, at least about 0.27, at least about 0.30, at least about 0.33, or at least about 0.35. Loss factor is measured by Mechanical Impedance Measurement as described in ISO Standard 16940. A polymer sample is laminated between two sheets of clear glass, each having a thickness of 2.3 mm, and is prepared to have a width of 25 mm and a length of 300 mm. The laminated sample is then excited at the center point using a vibration shaker, commercially available from Brüel and Kjær (Nærum, Netherlands) and an impedance head (Brüel and Kjær) is used to measure the force required to excite the bar to vibrate and the velocity of the vibration. The resultant transfer function is recorded on a National Instrument data acquisition and analysis system and the loss factor at the first vibration mode is calculated using the half power method. In some embodiments, when the RI balancing agent is a high RI plasticizer, the layer or interlayer may have a loss factor greater than 0.25, greater than 0.27, greater than 0.30, or greater than 0.35 at 20° C., while, in other embodiments, when the RI balancing agent is a solid RI additive or residues of at least one high RI aldehyde, the layer or interlayer may have a loss factor of at least about 0.10, at least about 0.15, at least about 0.20, at least about 0.25, or at least about 0.30 at 20° C.

“Sound transmission loss” (STL) is determined for a laminate of the present invention or comparative panel of fixed dimensions with ASTM E90 (2009) at a fixed temperature of 20° C. A “Reference Panel” of 2.3 mm clear glass//“Reference interlayer”//2.3 mm clear glass is measured to have STL of 31 dB at the coincident frequency (3,150 Hz), wherein the “Reference Interlayer” is produced by mixing and melt-extruding 100 parts poly(vinyl butyral) resin having a residual hydroxyl content of 18 to 19 wt. % and a vinyl acetate residue of 2 wt. %, 38 parts by weight of 3GEH plasticizer, and other common additives (as described above). The reference interlayer has a thickness of 0.76 mm and a glass transition temperature of 30° C. The interlayers of the present invention or the comparative interlayers are laminated with 2.3 mm clear glass according to the method described above for making the reference (or test) laminated glass panel. The panel has dimensions of 50 cm by 80 cm. The STL of the test panel at the coincident frequency of the “Reference Panel” (e.g., STL at 3,150 Hz) is used to assess the sound insulation property of the panel.

Similar to the resin blend of two distinct resins of the first poly(vinyl acetal) resin and the second poly(vinyl acetal) resin, blending two or more distinct resin layers or interlayers can often result in the new resin layer(s) or interlayer(s) having unexpected properties and performance attributes. For example, a resin layer or interlayer having lower residual hydroxyl content and lower glass transition temperature may be blended with another resin layer or interlayer having higher residual hydroxyl content and higher glass transition temperature, resulting a new resin layer or interlayer having soft domains of lower glass transition temperature, which enhances its acoustic performance, and stiff domains of higher glass transition temperature, which imparts enhanced processability, strength, and impact resistance to the resin layer or interlayer. Other example includes blending a single sheet interlayer and multilayer interlayer, blending two multilayer interlayers, or blending one multilayer interlayer into a resin layer of another multilayer interlayer. In essence, the effect arising from blending two materials can also be achieved from blending two or more resins, plasticizers, and other additives according to the contents of the materials. As used herein, a “blend resin material” or “blend material” refers to the resin composition, resin layer or interlayer to be blended into another resin composition, resin layer or interlayer. In blending two resin layers or two interlayers, at least one of the two materials to be blended can include the resin layer or interlayer of the present invention. In other embodiments, both materials can include the resin layers or interlayers of the present invention.

According to some embodiments, at least a portion of the resin compositions, layers, or interlayers described herein may comprise another resins, layers, or interlayers. In some embodiments, at least about 0.5, at least about 1, at least about 5, at least about 10, at least about 15, at least about 20, at least about 25, at least about 30, or at least about 50 percent of the total amount of resin in a composition, layer, or interlayer can originate from a blend resin material.

Often, when the type and/or amount of resins and plasticizers in the blend resin material differ substantially from the type and/or amount of the resin or plasticizer being produced, and into which the blend resin material is being added, the optical performance, as determined by the clarity or haze, of the resulting resin composition, layer, or interlayer that includes the blend resin material may be adversely impacted. According to embodiments of the present invention, resin layers and interlayers that include higher levels of blend resin material can be produced by utilizing one or more of the RI balancing agents discussed above.

When the RI balancing agent includes a high RI plasticizer, higher amounts of blend resin materials can be added to a process for producing a resin composition, layer, or interlayer described herein without reducing the clarity or increasing the haze of the final composition, layer, or interlayer. In some embodiments, the composition that includes blend materials can include a first poly(vinyl acetal) resin and a second poly(vinyl acetal) resin, wherein one of the resins has a residual hydroxyl content that can be at least 2 weight percent lower than the residual hydroxyl content of the other resin. Such a composition may further include at least one high RI plasticizer having a refractive index of 1.460, and, in some embodiments, more than 3 percent of the combined amount of the first and second poly(vinyl acetal) resins present in the composition, layer, or interlayer may have originated from a blend composition, layer, or interlayer. Despite the difference in residual hydroxyl contents of the first and second poly(vinyl acetal) resins, the composition that includes more than 0.5 weight percent of blend resin materials may have a haze value of not more than about 5, not more than about 4, not more than about 3, not more than about 2, or not more than about 1, or not more than about 0.5.

The high RI plasticizer used as an RI balancing agent with blend resin compositions can have a refractive index within one or more of the ranges described previously. The high RI plasticizer may be added during production of the composition, layer, or interlayer along with the blend material and/or at least a portion of the high RI plasticizer may be present in the blend resin material added to the process. Additionally, one or more other plasticizers may also be present in the resin material being blended and/or in the resin composition, layer, or interlayer being produced, including, for example, those having a refractive index less than about 1.450, less than about 1.445, or less than about 1.442, measured as described previously. In some embodiments, one or more additional high RI plasticizers may also be present in the blend material and/or in the resin composition, layer, or interlayer into which the materials are being blended.

The resin composition that includes blended resin material as described above can be used to form layers and interlayers according to various embodiments of the present invention. For example, the resin composition including a blend resin material can be used to form a single monolithic interlayer, or it may be used to form one or more layers of a multilayer interlayer. When used in various layers and interlayers, additional plasticizer may be added such that the total amount of plasticizer present in the resin layer or interlayer can be within the range described previously. Similarly, the glass transition temperature and refractive indices of resin layers and interlayers formed from a composition that includes a blend resin material may also be within the ranges provided above. Additionally, resin layers and interlayers formed from a composition that includes blended materials may also exhibit acoustic properties as described previously and may be included in any of the applications described below.

According to some embodiments, at least a portion of the resin compositions, layers, or interlayers described herein may comprise one or more recycled resin materials, including, for example, recycled layers or interlayers. As used herein, the term “recycled” means removed from and subsequently returned to a production line. Often, utilizing recycled materials may adversely affect the optical performance of the final composition, layer, or interlayer, as determined by clarity or haze, because of the different compositions and properties of the materials being blended or combined. However, in some embodiments, layers or interlayers as described herein may include at least one recycled resin material, while still exhibiting the same optical and/or acoustic properties as described herein. The type and/or amount of recycle resin material may fall within one or more of the ranges described previously and the layer or interlayer may further include at least one RI balancing agent. Additionally, the resin layers and interlayers including recycled resin material may also have optical and/or acoustic performance within one or more of the ranges described below.

The resin compositions, layers, and interlayers described above may be produced according to any suitable method. In various embodiments, the method for producing these compositions, layers, and interlayers can include providing two or more poly(vinyl acetal) resins, blending at least one resin with an RI balancing agent and, optionally, at least one plasticizer or other additive, to form a blended composition, and forming a layer from the blended composition.

In some embodiments, the resins provided in the initial steps of the method can be in the form of one or more poly(vinyl acetal) resins, while, in other embodiments, one or more resin precursors can also be provided. In some embodiments, when two or more poly(vinyl acetal) resins are physically blended, the blending of the two resins can comprise melt blending and may be performed at a temperature of at least about 140, at least about 150, at least about 180, at least about 200, at least about 250° C. In other embodiments, when the poly(vinyl acetal) resin components provided include resin precursors, the blending step may include reacting two or more aldehydes with a polyvinyl alcohol to provide a single poly(vinyl acetal) resin having two or more aldehyde moieties. Additionally, a portion of the blending step can include blending one or more of the resins with at least one plasticizer and/or with one or more of the RI balancing agents described previously.

The resulting blended resins can then be formed into one or more resin layers according to any suitable method. Exemplary methods of forming polymer layers and interlayers can include, but are not limited to, solution casting, compression molding, injection molding, melt extrusion, melt blowing, and combinations thereof. Multilayer interlayers including two or more resin layers may also be produced according to any suitable method such as, for example, co-extrusion, blown film, melt blowing, dip coating, solution coating, blade, paddle, air-knife, printing, powder coating, spray coating, and combinations thereof. In various embodiments of the present invention, the layers or interlayers may be formed by extrusion or co-extrusion. In an extrusion process, one or more thermoplastic polymers, plasticizers, and, optionally, at least one additive, including one or more RI balancing agents as described previously, can be pre-mixed and fed into an extrusion device. Other additives, such as ACAs, colorants, and UV inhibitors, which can be in liquid, powder, or pellet form, may also be used and may be mixed into the thermoplastic polymers or plasticizers prior to entering the extrusion device. These additives can be incorporated into the polymer resin and, by extension, the resultant polymer sheet, thereby enhancing certain properties of the polymer layer or interlayer and its performance in the final multiple layer glass panel or other end product.

In various embodiments, the thickness, or gauge, of the layers or interlayers can be at least about 10, at least about 15, at least about 20 mils and/or not more than about 100, not more than about 90, not more than about 60, not more than about 50, or not more than about 35 mils, or it can be in the range of from about 10 to about 100, about 15 to about 60, or about 20 to about 35 mils. In millimeters, the thickness of the polymer layers or interlayers can be at least about 0.25, at least about 0.38, at least about 0.51 mm and/or not more than about 2.54, not more than about 2.29, not more than about 1.52, or not more than about 0.89 mm, or in the range of from about 0.25 to about 2.54 mm, about 0.38 to about 1.52 mm, or about 0.51 to about 0.89 mm. In some embodiments, the resin layers or interlayers can comprise flat polymer layers having substantially the same thickness along the length, or longest dimension, and/or width, or second longest dimension, of the sheet, while, in other embodiments, one or more layers of a multilayer interlayer, for example, can be wedge-shaped or can have a wedge-shaped profile, such that the thickness of the interlayer changes along the length and/or width of the sheet, such that one edge of the layer or interlayer has a thickness greater than the other. When the interlayer is a multilayer interlayer, at least one, at least two, or at least three of the layers of the interlayer can be wedge-shaped. When the interlayer is a monolithic interlayer, the polymer sheet can be flat or wedge shaped. Wedge-shaped interlayers may be useful in, for example, heads-up-display (HUD) panels in automotive and aircraft applications.

The resin compositions, layers, and interlayers according to embodiments of the present invention may be utilized in a multiple layer panel that comprises a resin layer or interlayer and at least one rigid substrate. Any suitable rigid substrate may be used and in some embodiments may be selected from the group consisting of glass, polycarbonate, biaxially oriented PET, copolyesters, acrylic, and combinations thereof. When the rigid substrate includes glass, the glass can be selected from the group listed previously. When the rigid substrate includes a polymeric material, the polymeric material may or may not include a hard coat surface layer. In some embodiments, the multilayer panels include a pair of rigid substrates with the resin interlayer disposed there between. The panels can be used for a variety of end use applications, including, for example, for automotive windshields and windows, aircraft windshields and windows, panels for various transportation applications such as marine applications, rail applications, etc., structural architectural panels such as windows, doors, stairs, walkways, balusters, decorative architectural panels, weather-resistant panels, such as hurricane glass or tornado glass, ballistic panels, and other similar applications.

When laminating the resin layers or interlayers between two rigid substrates, such as glass, the process can include at least the following steps: (1) assembly of the two substrates and the interlayer; (2) heating the assembly via an IR radiant or convective device for a first, short period of time; (3) passing the assembly into a pressure nip roll for the first de-airing; (4) heating the assembly for a short period of time to about 60° C. to about 120° C. to give the assembly enough temporary adhesion to seal the edge of the interlayer; (5) passing the assembly into a second pressure nip roll to further seal the edge of the interlayer and allow further handling; and (6) autoclaving the assembly at temperature between 135° C. and 150° C. and pressures between 150 psig and 200 psig for about 30 to 90 minutes. Other methods for de-airing the interlayer-glass interface, as described according to some embodiments in steps (2) through (5) above include vacuum bag and vacuum ring processes, and both may also be used to form interlayers of the present invention as described herein.

In some embodiments, the multiple layer panel may include at least one polymer film disposed on the layer or interlayer, forming a multiple layer panel referred to as a “bilayer.” In some embodiments, the interlayer utilized in a bilayer may include a multilayer interlayer, while, in other embodiments, a monolithic interlayer may be used. The use of a polymer film in multiple layer panels as described herein may enhance the optical character of the final panel, while also providing other performance improvements, such as infrared absorption. Polymer films differ from polymer layers or interlayers in that the films alone do not provide the necessary penetration resistance and glass retention properties. The polymer film can also be thinner than the sheet, and may have a thickness in the range of from 0.001 to 0.25 mm. Poly(ethylene terephthalate) (“PET”) is one example of a material used to form the polymer film.

The following examples are intended to be illustrative of the present invention in order to teach one of ordinary skill in the art to make and use the invention and are not intended to limit the scope of the invention in any way.

EXAMPLES

The following Examples describe the preparation of several resin compositions, layers, and interlayers that include various poly(vinyl acetal) reins. As described below, several tests performed on many of the compositions, layers, and interlayers were used to evaluate the acoustic and optical properties of several comparative and inventive materials.

Example 1 Preparation of High Refractive Index Poly(Vinyl Acetal) Resins

Several comparative poly(vinyl acetal) resins, referred to as Comparative Resins CR-1 through CR-12 in Table 2 below, were prepared by acetalizing polyvinyl alcohol with one or more aldehydes including n-butyraldehyde (nBuCHO; RI=1.377), iso-butyraldehyde (iBuCHO; RI=1.374), and 2-ethylhexyl aldehyde (2EHCHO; RI=1.414). The composition of the resulting resins were measured using either the ASTM D1396 or FT-IR/SEC method described in detail previously. The refractive index of several of the resins was also measured according to the methods described previously, and the results are provided in Table 2, below.

TABLE 2 Properties of Several Comparative Poly(vinyl acetal) Resins Resi- Resin dual Resi- Residual Residual Residual Refrac- Hydrox- dual Polyvinyl Polyvinyl Polyvinyl tive yl Acetate nBuCHO iBuCHO 2EHCHO Index Resin (wt %) (wt %) (wt %) (wt %) (wt %) (nD25) CR-1 21 1 78 — — 1.491 CR-2 19 1 80 — — 1.490 CR-3 19 1 46 — 34 1.489 CR-4 16 1 83 — — 1.488 CR-5 15 1 39 — 45 1.487 CR-6 13 1 86 — — 1.486 CR-7 12 18 70 — — 1.481 CR-8 12 12 76 — — nd CR-9 12 10 78 — — 1.483 CR-10 11 1 88 — — 1.485 CR-11 12 1 — 88 — nd CR-12 13 1 — 86 — nd nd = not determined

Additionally, several poly(vinyl acetal) resins according to embodiments of the present invention were also prepared in a similar manner. These inventive resins, referred to as Disclosed Resins DR-1 through DR-21 in Table 3, were formed by acetalizing polyvinyl alcohol with mixtures of n-butyraldehyde and various high refractive index aldehydes, including benzaldehyde (BzCHO RI=1.545), cinnamaldehyde (CCHO; RI=1.620), 4-chlorobenzaldehyde (4-CIBzCHO; RI=1.585), 2-phenylpropionaldehyde (2PHPrCHO; RI=1.517), and hydrocinnamaldehyde (HCCHO; RI=1.523). The refractive index of several of the Disclosed Resins was also determined and the results are summarized in Table 3, below.

TABLE 3 Properties of Disclosed Resins Resin Residual Residual Aldehyde HCCHO/ CCHO/ 2PhPrCHO/ BzCHO/ 4ClBzCHO/ Refractive Hydroxyl Acetate Component BuCHO BuCHO BuCHO BuCHO BuCHO HCCHO/ Index Resin (wt %) (wt %) (wt %) (mol/mol) (mol/mol) (mol/mol) (mol/mol) (mol/mol) iBuCHO (nD25) DR-1 11 1 88  5/95 — — — — — 1.496 DR-2 11 1 88 10/90 — — — — — 1.500 DR-3 11 1 88 15/85 — — — — — 1.504 DR-4 11 1 88 20/80 — — — — — 1.510 DR-5 11 1 88 25/75 — — — — — 1.511 DR-6 11 1 88 50/50 — — — — — 1.528 DR-7 11 1 88 100/0  — — — — — 1.552 DR-8 19 1 80 10/90 — — — — — nd DR-9 19 1 80 25/75 — — — — — nd DR- 19 1 80 50/50 — — — — — nd 10 DR- 19 1 80 100/0  — — — — — nd 11 DR- 12 18 70 25/75 — — — — — nd 12 DR- 12 10 78 25/75 — — — — — nd 13 DR- 17 1 82 — 25/75 — — — — 1.507 14 DR- 15 1 84 — — 25/75 — — — 1.505 15 DR- 14 1 85 — — 25/75 — — — 1.503 16 DR- 18 1 81 — — — 25/75 — — 1.507 17 DR- 14 1 85 — — — 25/75 — — 1.501 18 DR- 20 1 79 — — — — 25/75 — 1.507 19 DR- 14 1 85 — — — — 25/75 — 1.509 20 DR- 11 1 88 — — — — — 25/75 nd 21 nd = not determined

As shown in Tables 2 and 3, above, polyvinyl acetal resins comprising residues of at least one high refractive index aldehyde, including those listed above, tend to exhibit higher refractive indices than those comprising residues of aldehydes such as n-butyraldehyde, iso-butyraldehyde, and 2-ethylhexyl aldehyde.

Example 2 Preparation of High Refractive Index Resin Interlayers

Several Comparative and Disclosed Interlayers were formed by mixing and melt blending several of the Comparative Resins listed in Table 2 and several of the Disclosed Resins listed in Table 3 above, with varying amounts of the plasticizer triethylene glycol bis(2-ethylhexanoate) (3GEH). The composition, refractive index, and glass transition temperature of each of the resulting interlayers, referred to as Comparative Interlayers CL-1 through CL-14 and Disclosed Interlayers DL-1 through DL-26, were measured as described previously, and the results are respectively summarized in Tables 4 and 5, below.

TABLE 4 Properties of Several Comparative Interlayers Refractive Plasticizer Index T_(g) Interlayer Resin (phr) (nD25) (° C.) CL-1 CR-1 34 1.478 36 CL-2 CR-2 38 1.477 30 CL-3 CR-3 38 1.475 28 CL-4 CR-4 50 1.472 17 CL-5 CR-4 30 1.477 30 CL-6 CR-5 75 1.468 6 CL-7 CR-6 75 1.467 2 CL-8 CR-7 75 1.464 −4 CL-9 CR-8 75 1.466 −3 CL-10 CR-9 75 1.465 −3 CL-11 CR-10 75 1.466 −2 CL-12 CR-10 50 1.47 12 CL-13 CR-11 75 nd nd CL-14 CR-12 75 nd nd nd = not determined

TABLE 5 Properties of Several Disclosed Interlayers Sheet Plasticizer Refractive content Index T_(g) Interlayer Resin (phr) (nD25) (° C.) DL-1 DR-1 75 1.473 1 DL-2 DR-1 50 1.479 12 DL-3 DR-2 75 1.475 0 DL-4 DR-3 75 1.477 0 DL-5 DR-4 75 1.480 1 DL-6 DR-5 75 1.482 1 DL-7 DR-6 75 1.490 2 DL-8 DR-7 75 1.506 3 DL-9 DR-14 75 1.480 12 DL-10 DR-15 75 1.478 11 DL-11 DR-16 75 1.477 7 DL-12 DR-17 75 1.480 22 DL-13 DR-18 75 1.476 12 DL-14 DR-19 75 1.480 17 DL-15 DR-20 75 1.479 12 DL-16 DR-12 75 nd nd DL-17 DR-13 75 nd nd DL-18 DR-21 75 nd nd DL-19 DR-8 38 1.477 30 DL-20 DR-9 38 1.487 nd DL-21 DR-10 38 1.501 nd DL-22 DR-11 38 1.525 nd DL-23 DR-5 38 nd nd DL-24 DR-5 50 1.488 nd DL-25 DR-5 60 1.484 2 DL-26 DR-7 38 nd nd nd = not determined

As shown in Tables 4 and 5, above, Disclosed Interlayers utilizing higher refractive index Disclosed Resins from Table 3 exhibit higher refractive indices than Comparative Interlayers formulated with lower refractive index resins, such as the Comparative Resins listed in Table 2. Additionally, as shown by comparison of Disclosed Interlayers DL-1 and DL-2 and DL-6 and DL-23 through DL-25, the amount of plasticizer used to form an interlayer affects both the glass transition temperature and refractive index of the layer, although not necessarily to the same extent for all resins. For example, as shown by the comparison of DL-1 (75 phr 3GEH; Disclosed Resin 1) and DL-2 (50 phr 3GEH; Disclosed Resin 1), reducing the amount of plasticizer by about 33 percent increases the glass transition temperature of the interlayer by 11° C. (from 1° C. to 12° C.), and increases the refractive index by 0.006 (from 1.473 to 1.479). However, as shown by the comparison of DL-25 (60 phr 3GEH; Disclosed Resin 5) and DL-6 (75 phr of 3GEH; Disclosed Resin 5), reducing the plasticizer content in layers formed by this resin increases the glass transition temperature by only 1° C. (from 1° C. to 2° C.), while increasing the refractive index by only 0.002 (from 1.482 to 1.484).

Example 3 Preparation of Interlayers Using High Refractive Index Resins

Several of the Comparative and Disclosed Interlayers formed in Example 2 and respectively summarized in Tables 4 and 5, above, were used to create several Comparative and Disclosed Multilayer Interlayers. Each multilayer interlayer included a pair of outer “skin” layers, having a total thickness of 28 mils, sandwiching an inner “core” layer having a thickness of 5 mils, usually formed of a resin having a lower residual hydroxyl content. The composition and several properties of the interlayers including refractive index, glass transition temperature, mottle, and loss factor, were measured as described above, and the results for the Comparative Multilayer Interlayers (CI-1 to CI-16) and Disclosed Multilayer Interlayers (DI-1 to DI-29) are summarized in Tables 6 and 7, below.

TABLE 6 Properties of Several Comparative Multilayer Interlayers Δ Refractive Refractive Index Index of Loss Resin Layer T_(g) (° C.) Refractive Index (Skin − Interlayer Factor at Interlayer Skin 1 Core Skin 2 Skin 1 Core Skin 2 Skin 1 Core Skin 2 Core) (nD25) Mottle 20° C. CI-1 CL-2 CL-7 CL-2 30 2 30 1.477 1.467 1.477 0.010 1.475 4 0.29 CI-2 CL-2 CL-11 CL-2 30 −2 30 1.477 1.466 1.477 0.011 1.475 5 0.33 CI-3 CL-2 CL-8 CL-2 30 −4 30 1.477 1.464 1.477 0.013 1.475 5 nd CI-4 CL-1 CL-9 CL-1 36 −3 36 1.478 1.466 1.478 0.012 1.477 5 nd CI-5 CL-1 CL-8 CL-1 36 −4 36 1.478 1.464 1.478 0.014 nd 5 0.36 CI-6 CL-2 CL-9 CL-2 30 −3 30 1.477 1.466 1.477 0.011 nd 5 nd CI-7 CL-1 CL-11 CL-1 36 −2 36 1.478 1.466 1.478 0.012 1.477 5 0.35 CI-8 CL-2 CL-10 CL-2 30 −3 30 1.477 1.465 1.477 0.012 nd 5 0.31 CI-9 CL-1 CL-7 CL-1 36 2 36 1.478 1.467 1.478 0.011 nd 5 nd CI-10 CL-1 CL-10 CL-1 36 −3 36 1.478 1.465 1.478 0.013 nd 5 nd CI-11 CL-2 CL-13 CL-2 30 nd 30 nd nd nd nd nd >5 nd CI-12 CL-2 CL-14 CL-2 30 nd 30 nd nd nd nd nd >5 nd CI-13 CL-1 CL-13 CL-1 36 nd 36 nd nd nd nd nd >5 nd CI-14 CL-1 CL-14 CL-1 36 nd 36 nd nd nd nd nd >5 nd CI-15 CL-2 DL-7 CL-2 30 2 30 1.477 1.490 1.477 −0.013 1.479 >5 nd CI-16 CL-2 DL-8 CL-2 30 3 30 1.477 1.506 1.477 −0.029 1.481 >5 nd nd = not determined

TABLE 7 Properties of Some Disclosed Multilayer Interlayers Δ Refractive Refractive Index Index Refractive Resin Layer T_(g) (° C.) (nD25) (Skin − Index of Interlayer Skin 1 Core Skin 2 Skin 1 Core Skin 2 Skin 1 Core Skin 2 Core) Interlayer Mottle DI-1 CL-2 DL-1 CL-2 30 1 30 1.477 1.473 1.477 0.004 1.476 1 DI-2 CL-2 DL-4 CL-2 30 0 30 1.477 1.477 1.477 0.000 1.477 1 DI-3 CL-5 DL-6 CL-5 30 1 30 1.477 1.482 1.477 −0.005 1.478 nd DI-4 CL-2 DL-6 CL-2 30 1 30 1.477 1.482 1.477 −0.005 nd <1 DI-5 CL-1 DL-6 CL-1 36 1 36 1.478 1.482 1.478 −0.004 nd <1 DI-6 CL-2 DL-3 CL-2 30 0 30 1.477 1.475 1.477 0.002 nd <1 DI-7 CL-2 DL-5 CL-2 30 1 30 1.477 1.480 1.477 −0.003 nd <1 DI-8 CL-2 DL-6 CL-1 30 1 36 1.477 1.482 1.478 −0.005 nd <1 DI-9 CL-2 DL-6 CL-5 30 1 30 1.477 1.482 1.477 −0.005 nd <1 DI-10 CL-2 DL-16 CL-2 30 nd 30 1.477 nd 1.477 nd nd <1 DI-11 CL-2 DL-17 CL-2 30 nd 30 1.477 nd 1.477 nd nd <1 DI-12 CL-1 DL-16 CL-1 36 nd 36 1.478 nd 1.478 nd nd <1 DI-13 CL-1 DL-17 CL-1 36 nd 36 1.478 nd 1.478 nd nd <1 DI-14 CL-2 DL-18 CL-2 30 nd 30 1.477 nd 1.477 nd nd <1 DI-15 CL-1 DL-18 CL-1 36 nd 36 1.478 nd 1.478 nd nd <1 DI-16 DL-19 DL-24 DL-19 30 1 30 1.477 1.488 1.477 −0.005 1.478 <1 DI-17 CL-2 DL-9 CL-2 30 12 30 1.477 1.480 1.477 −0.003 nd <1 DI-18 CL-2 DL-10 CL-2 30 11 30 1.477 1.478 1.477 −0.001 nd <1 DI-19 CL-2 DL-11 CL-2 30 7 30 1.477 1.477 1.477 0.000 nd <1 DI-20 CL-2 DL-12 CL-2 30 22 30 1.477 1.480 1.477 −0.003 nd <1 DI-21 CL-2 DL-13 CL-2 30 12 30 1.477 1.476 1.477 0.001 nd <1 DI-22 CL-2 DL-14 CL-2 30 17 30 1.477 1.480 1.477 −0.003 nd <1 DI-23 CL-2 DL-15 CL-2 30 12 30 1.477 1.479 1.477 −0.002 nd <1 DI-24 DL-20 DL-7 DL-20 nd 2 nd 1.487 1.490 1.487 −0.003 nd <1 DI-25 DL-21 DL-7 DL-21 nd 2 nd 1.501 1.490 1.501 −0.011 nd >5 DI-26 DL-22 DL-7 DL-22 nd 2 nd 1.525 1.490 1.525 −0.035 nd >5 DI-27 DL-20 DL-8 DL-20 nd 3 nd 1.487 1.506 1.487 −0.009 nd 3 DI-28 DL-21 DL-8 DL-21 nd 3 nd 1.501 1.506 1.501 −0.005 nd <1 DI-29 DL-22 DL-8 DL-22 nd 3 nd 1.525 1.506 1.525 −0.019 nd >5 nd = not determined

As shown in Table 6, above, interlayers formed from skin and core layers having refractive index differences of 0.010 or more exhibited optical defects, as indicated by the mottle values greater than 5. As shown in Table 7, however, interlayers formed from skin and core layers having refractive index differences of less than 0.010 exhibited low mottle values of 1 or less. Additionally, as shown in Table 7, such low mottle values were achievable by interlayers having a core layer with a higher or lower refractive index than the skin layer, as long as the absolute value of the difference between the refractive indices of adjacent layers was less than 0.010. Also as shown in Table 7, interlayers formed from skin and core layers both having high RI aldehyde residues and having refractive index differences of greater than 0.010 exhibited high mottle values of 5 or greater.

Example 4 Stability of Multilayer Interlayers

Two Comparative Multilayer Interlayers, CI-2 and CI-7, and two Disclosed Multilayer Interlayers, DI-4 and DI-5, prepared as described in Examples 1-3 above, were tested to determine the relative stability of the interlayers over time. Net plasticizer migration, which was measured by comparing the glass transition temperatures of each layer at an initial time (t=0) and after the layers have achieved equilibrium. The results are summarized in Table 8, below.

TABLE 8 Net Plasticizer Migration and Properties of Exemplary Comparative and Disclosed Interlayers T_(g) at Δ T_(g) at t = 0 Equilibrium Refractive (° C.) (° C.) ΔT_(g) (° C.) Index Inter- T_(g) T_(g) T_(g) T_(g) ΔT_(g) ΔT_(g) (Skin − layer Skin Core Skin Core Skin Core Core) Mottle CI-2 36 4.2 36 4.6 0.0 0.4 0.011 >5 DI-4 36 1.4 36.4 1.4 0.4 0.0 −0.005 <1 CI-7 42.5 2.2 42.5 1.4 0.0 −0.8 0.012 >5 DI-5 40.9 0.2 41.7 −1.8 0.8 −2.0 −0.004 <1

Disclosed Interlayer DI-4 exhibited minimal changes in the glass transition temperature of both the skin and core layers of the interlayer at equilibrium. This indicates a minor amount of plasticizer migration between the skin and core layers of each of Interlayers CI-2, CI-7, and DI-4. Although Comparative Interlayers CI-2 and CI-7 may be relatively stable, both exhibited a mottle value greater than 5, which would be unacceptable for most optical applications. In contrast, the mottle value exhibited by Disclosed Interlayer DI-4 was less than 1.

The slight decrease in glass transition temperature exhibited by Disclosed Interlayer DI-5 at equilibrium indicated that a small amount of plasticizer migrated from the skin layer to the core layer. Such migration could be alleviated by utilizing a smaller amount of plasticizer in the skin layer or a larger amount in the core. Even so, the refractive index of the core layer and the skin layer of Disclosed Interlayer DI-5 differed by only 0.004 and, as a result, the interlayer also exhibited a mottle value less than 1.

Example 5 Blend of Conventional Poly(Vinyl Acetal) Resins and High Refractive Index Poly(Vinyl Acetal) Resins

Several Comparative and Disclosed Resins, prepared as described in Example 1 above, were mixed and melt-blended together with 38 phr of 3GEH plasticizer to form Comparative Blended Layers CBL-16 and CBL-17 and Disclosed Blended Layers DBL-27 and DBL-28. Comparative Resin Layer CL-2 is listed in Table 9. CL-15 was formulated with Comparative Resin CR-10 and 38 phr of 3GEH, while Disclosed Resin Layers DL-27 and DL-28 were formulated with Disclosed Resins DR-3 and DR-5, respectively, and 38 phr of 3GEH. The haze and percent visual transmittance (T_(vis)) for each blended resin interlayer were measured, along with the haze and percent visual transmittance. The results are provided in Table 9, below.

TABLE 9 Haze and Percent Visual Transmittance of Several Resin Layers nposition Property CR-2 DR-3 Plasticizer (wt CR-10 (wt DR-5 content Haze Interlayer %) (wt %) %) (wt %) (phr) (%) % T_(vis) CL-2 100  — — — 38 0.5 87.7 CL-15 — 100 — — 38 0.5 87.8 CBL-16 96  4 — — 38 2.1 84.3 CBL-17 89  11 — — 38 14.7 80.2 DBL-27 96 —  4 — 38 0.8 87.8 DBL-28 89 — —  11 38 0.6 87.8 DL-27 — — 100 — 38 0.5 87.7 DL-28 — — — 100 38 0.5 87.8

As shown in Table 9 above, Comparative Blended Interlayers CBL-16 and CBL-17, which were formed from a blend of Comparative Resins CR-2 and CR-10, exhibited high haze values and lower percent visual transmittance than single resin layers of Comparative Resin CR-2 (Comparative Layer CL-2) or CR-10 (Comparative Interlayer CL-15). In contrast, Disclosed Blended Interlayers DBL-27 and DBL-28, which were formed from a blend of Comparative Resin CR-2 and a high refractive index Disclosed Resin (Resin DR-3 in Layer DBL-27 or Resin DR-5 in Layer DBL-28), exhibited substantially the same haze and percent visual transmittance as Comparative Interlayer CL-2, which was formulated with Comparative Resin CR-2 alone. Thus, addition of inventive high refractive index resins to a comparative interlayer does not reduce the optical quality of the resulting interlayer.

Example 6 Preparation of Interlayers Having High Refractive Index Additives

Several poly(vinyl acetal) resins were prepared by acetalizing polyvinyl alcohol with n-butyraldehyde. The resins, which had different residual hydroxyl contents, were melt blended with varying amounts of a 3GEH plasticizer and used to form various layers of multilayer interlayers. Each interlayer had an inner “core” layer having a thickness of 5 mils sandwiched between two outer “skin” layers, each having a thickness of 14 mils. The poly(vinyl butyral) resin used to form the core layers had a hydroxyl content of 11 weight percent and the resin used for the skin layers had a hydroxyl content of 19 weight percent. Both resins had a residual acetate content of about 2 weight percent.

Comparative Interlayers CI-17 through CI-19 were formed with resin layers plasticized with 3GEH, which was present in varying amounts in the core and skin layers. In addition to the 3GEH, Disclosed Interlayers DI-30 through DI-38 also included varying amounts of two different high refractive index additives, Benzoflex™ 2-45 (diethyleneglycol dibenzoate; commercially available from Eastman Chemical Company, Kingsport, Tenn.) (Additive A-1), which had a melting point of 28° C. and a refractive index of 1.542; and Benzoflex™ 352 (1,4-cyclohexane dimethanol dibenzoate; commercially available from Eastman Chemical Company) (Additive A-2), which had a melting point of 118° C. and a refractive index of 1.554. The refractive index and glass transition temperatures of each of the layers of Comparative Interlayers CI-17 through CI-19 and Disclosed Interlayers DI-30 through DI-38 were measured and the results are summarized in Table 10 below.

TABLE 10 Properties of Several Comparative and Disclosed Interlayers Skin Layers Core Layer Plasticizer High RI High RI Plasticizer High RI Δ Refractive Content Addi- Additive Total Content High RI Additive Index Inter- (P) tive (A) A + A:P T_(g) (P) Additive (A) Total A:P T_(g) (Skin − layer (phr) Type (phr) P Ratio RI (° C.) (phr) Type (phr) A + P Ratio RI (° C.) Core) CI-17 40 — — — 1.476 30 65.0 — — — 1.467 2.9 0.008 CI-18 40 — — — 1.476 30 75.0 — — — 1.466 −2.0 0.010 CI-19 40 — — — 1.476 30 85.0 — — — 1.465 −3.1 0.011 DI-30 20 A-1 20 40 1.0 1.492 29 32.5 A-1 32.5 65 1.0 1.488 4.2 0.004 DI-31 20 A-1 20 40 1.0 1.492 29 37.5 A-1 37.5 75 1.0 1.488 −0.6 0.004 DI-32 20 A-1 20 40 1.0 1.489 29 42.5 A-1 42.5 85 1.0 1.488 −3.3 0.004 DI-33 17.2 A-1 22.8 40 1.3 1.496 30 22.8 A-1 42.2 65 1.9 1.494 5.2 0.002 DI-34 17.2 A-1 22.8 40 1.3 1.496 30 26.2 A-1 48.8 75 1.9 1.494 2.4 0.002 DI-35 17.2 A-1 22.8 40 1.3 1.496 30 29.8 A-1 55.2 85 1.9 1.494 −2.1 0.002 DI-36 20 A-2 20 40 1.0 1.493 34 27.5 A-2 27.5 55 1.0 1.490 15.9 0.003 DI-37 20 A-2 20 40 1.0 1.493 34 35.0 A-2 35.0 70 1.0 1.490 8.4 0.003 DI-38 20 A-2 20 40 1.0 1.493 34 42.5 A-2 42.5 85 1.0 1.491 1.8 0.002

As shown in Table 10, above, increasing the plasticizer content of the core layer of an interlayer that only included a 3GEH plasticizer reduced the glass transition temperature of the layer, which, ultimately, would have improved its acoustic performance. However, such an increase also widened the difference between the refractive indices of the skin and core layers, thereby reducing the optical quality of the interlayer. As shown by comparison with Disclosed Interlayers DI-30 through DI-38 in Table 10, the refractive index of core layers formulated with an additional high refractive index additive, remained fairly constant with increased plasticizer loading, while still exhibiting a similar reduction in glass transition temperature. The result was an interlayer having core and skin layers with nearly the same refractive index, which greatly reduced optical defects such as mottle. At the same time, the core layer also exhibited a sufficiently low glass transition temperature, indicating that the core layer also had acoustic properties.

Example 7 Preparation of Core Layers Having Reactive High Refractive Index Additives

Several resin layers, used to simulate the inner core layer of a multilayer interlayer, were formed by melt blending a polyvinyl n-butyral resin having a residual hydroxyl content of 11 weight percent and a residual acetate content of about 2 weight percent with varying amounts of 3GEH plasticizer. Comparative Layer CL-16 included 75 phr of 3GEH, while Disclosed Layers DL-29 through DL-31 were formulated with various mixtures of 3GEH and a reactive high refractive index additive (reactive high RI additive). The reactive high RI additive used in Disclosed Layers DL-29 and DL-30 (Additive A) was diphenyldimethoxysilane (commercially available as SID4535.0 from Gelest, Inc., Morrisville, Pa.), and the reactive high RI additive used in Disclosed Layer DL-31 (Additive B) was phthalic anhydride (commercially available from Sigma Aldrich Co., St. Louis, Mo.). The refractive index of Comparative Layer CL-16 and each of Disclosed Layers DL-29 through DL-31 was measured and the results are provided in Table 11, below.

TABLE 11 Refractive Index of Comparative and Disclosed Core Resin Layers Plasticizer Additive A Additive B Resin Content Content Content Refractive Index Layer (phr) (phr) (phr) (nD25) CL-16 75 — — 1.466 DL-29 72 3 — 1.468 DL-30 72 6 — 1.470 DL-31 72 — 3 1.470

As shown in Table 11, resin layers formed using 3GEH in combination with one or more reactive high refractive index additives had a higher refractive index than resin layers formulated with only 3GEH. As a result, when employed as an inner core layer in a multilayer interlayer, the Disclosed Layers DL-29 through DL-31 had a refractive index that more closely matched the refractive index of a skin layer formed of polyvinyl n-butyral (RI=1.477). As a result, multilayer interlayers formed with Disclosed Layers DL-29 through DL-31 as a core layer exhibit fewer optical defects than multilayer interlayers formed with Comparative Layer CL-16 as an inner core layer.

Example 8 Various Interlayers with Resin Blends Having a High Refractive Index Plasticizer

Two polyvinyl n-butyral resins, R-1 and R-2, were prepared according to the procedure described above in Example 1. Resin R-1 had a residual hydroxyl content of 19 weight percent, while resin R-2 had a residual hydroxyl content of 11 weight percent. Both resins had residual acetate contents of 2 weight percent. Several resin blends were prepared that included varying amounts of resins R-1 and R-2 in order to simulate various blending rates. The blends were combined with 38 phr of a plasticizer selected from 3GEH (plasticizer P-1; RI=1.442), dioctyl phthalate (plasticizer P-2; RI=1.485), a blend of 30 weight percent 3GEH and 70 weight percent Benzoflex® 2088, which is commercially available from Eastman Chemical Company, Kingsport, Tenn., (plasticizer P-3; RI=1.506), and nonylphenyl tetraethylene glycol (plasticizer P-4; RI=1.500). The resulting plasticized resins were then formed into single sheets that included both resins and the plasticizer. The refractive index, haze, and percent visual transmittance was determined for each sheet and the results are provided in Table 12, below.

TABLE 12 Properties of Several Resin Blends Plasticizer P-1 Plasticizer P-2 Plasticizer P-3 Plasticizer P-4 Resin A Resin B RI of Haze T_(vis) RI of Haze T_(vis) RI of Haze T_(vis) RI of Haze T_(vis) (wt %) (wt %) Interlayer (%) (%) Interlayer (%) (%) Interlayer (%) (%) Interlayer (%) (%) 100 0 1.477 0.4 88.5 1.494 0.4 88.5 1.495 0.3 88.4 1.493 0.3 88.5 98.9 1.1 1.477 0.6 87.9 1.494 0.4 88.6 1.495 0.3 88.8 1.493 0.3 88.7 97.8 2.2 1.476 1.2 87.1 1.498 0.3 88.4 1.495 0.3 88.7 1.493 0.2 88.7 95.6 4.4 1.477 1.9 84.6 1.495 0.4 88.4 1.495 0.3 88.6 1.492 0.4 88.5 91.2 8.8 1.476 5.4 81.7 1.495 0.5 88.3 1.495 0.4 88.5 1.493 0.3 88.6 88.9 11.1 1.476 12.9 80.6 1.494 0.6 88.2 1.495 0.4 88.2 1.492 0.4 88.2

As shown in Table 12, above, although blended resin layers formulated with plasticizer P-1 maintained a substantially constant refractive index with increasing amounts of the lower hydroxyl content resin R-2, the optical properties of these resin blends having high levels of R-2 worsened as the amount of R-2 increased. For example, as shown in Table 12, the haze of blends that included more than 1.1 percent of resin R-2 increased, while the percent visual transmittance of these blends decreased from 88.5 percent to 80.6 percent.

In contrast, the resin blends including more than 2.2 percent of resin R-2 that were plasticized with higher refractive index plasticizers P-2 through P-4, each exhibited substantially the same haze value and percent visual transmittance as blends having lower amounts of resin R-2. Therefore, it can be concluded that the resin blends utilizing higher refractive index plasticizers, such as plasticizers P-2 through P-4, may permit higher amounts of lower hydroxyl content resins without adversely impacting the optical properties of the final blend.

Example 9 Poly(Vinyl Butyral) Layers Including a High Refractive Index Plasticizer

Several poly(vinyl n-butyral) layers were formed by combining and melt blending three different poly(vinyl n-butyral) resins (PVB-1 through PVB-3) with different types and amounts of plasticizer. Each of the resins PVB-1 through PVB-3 had a different residual hydroxyl content, ranging from 11 to 20.4 weight percent, and all three resins had a residual vinyl acetate content of 1 weight percent. Comparative Layers CL-17 through CL-19 were formulated with varying amounts of triethylene glycol di-(2-ethylhexanoate) (“3GEH”; RI=1.442), while Disclosed Layers DL-32 through DL-37 included a mixture of 3GEH with Benzoflex™ 354 (commercially available from Eastman Chemical Company, Kingsport, Tenn.)(RI=1.53). The refractive index of each layer was measured and the results are summarized in Table 13, below.

TABLE 13 Several Poly(vinyl) Butyral Layers with Various Plasticizers Plasticizer Content Residual Ratio of hydroxyl 3GEH Benzoflex ™ 3GEH to Total plasticizer Refractive Resin content content 354 Benzoflex ™ content Index Layer (wt %) (phr) (phr) 354 (phr) (nD25) CL-17 19 38 — — 38 1.477 CL-18 19 38 — — 38 1.477 CL-19 11 75 — — 38 1.466 DL-32 20.4 30.1 12.9 30/70 43 1.484 DL-33 20.4 25.8 17.2 40/60 43 1.485 DL-34 20.4 21.5 21.5 50/50 43 1.488 DL-35 11 59.5 25.5 30/70 85 1.479 DL-36 11 51 34 40/60 85 1.481 DL-37 11 42.5 42.5 50/50 85 1.486

As shown in Table 13, above, resin layers that included a high refractive index plasticizer exhibited a higher refractive index than those that included only a low refractive index plasticizer.

Example 10 Preparation of Interlayers Having High Refractive Index Additives

Several of the Comparative and Disclosed Interlayers formed in Example 9 and summarized in Table 13, above, were used to create several Comparative and Disclosed Multilayer Interlayers. Each multilayer interlayer included a pair of outer “skin” layers, each having a thickness of 14 mils, sandwiching an inner “core” layer, having a thickness of 5 mils, formed of a resin having a lower residual hydroxyl content. The composition and several properties of the multilayer interlayers, including total plasticizer content, refractive index, glass transition temperature, mottle, and loss factor, were measured as described above, and the results for the Comparative Multilayer Interlayers CI-20 and CI-21 and Disclosed Multilayer Interlayers DI-39 through DI-41 are summarized in Table 14, below.

TABLE 14 Properties of Several Comparative and Disclosed Interlayers Δ Total Refractive plasticizer Index Refractive T_(g) Loss Interlayer Skin Core Skin content (Skin − Index (° C.) Factor at No Layer 1 Layer Layer 2 (phr) Core (nD25) Skin Core Mottle 20° C. CI-20 CL-17 CL-18 CL-17 38 0.000 1.477 30 — 0 0.02 CI-21 CL-17 CL-19 CL-17 42.5 0.011 1.475 35 3 5 0.32 DI-39 DL-32 DL-35 DL-32 48 0.005 1.484 38.8 2.6 0.4 0.41 DI-40 DL-33 DL-36 DL-33 48 0.004 1.486 39.6 4.7 0.4 0.39 DI-41 DL-34 DL-37 DL-34 48 0.002 1.488 40.9 8.7 0.4 0.33

As shown in Table 14 above, interlayers formed from skin and core layers having a refractive index difference greater than 0.010 exhibited more optical defects, as shown by the mottle value of 5. Additionally, Disclosed Interlayers D-39 through D-41, which utilized a high refractive index plasticizer, exhibited a higher overall refractive index as compared to Comparative Interlayers CI-20 and CI-21, which only utilized a plasticizer having a refractive index less than 1.460, the difference of refractive indices between skin and core is 0.005, and the mottle is 0.4

Example 11 Incompatible Terephthalic Acid Based Plasticizer with High Refractive Index

Di-2-ethylhexylterephthalate (DOTP) was used to make Disclosed Interlayers DL-38 through DL-47 in Table 16 below and these Disclosed Interlayers were used to make Disclosed Multilayer Interlayers, DI-42 to DI-46, also presented in Table 16 below.

TABLE 15 Abbreviations and Refractive Index of Several Plasticizers Plasticizer Chemical Name Refractive index (nD25) 3GEH triethylene glycol di-2-ethylhexanoate 1.442 DOP Dioctyl phthalate 1.485 DINP Diisononyl phthalate 1.485 DOTP Di-2-ethylhexyl terephthalate 1.489 METP Bis-(methoxyethyl) terephthalate 1.503 BETP Bis-(butoxyethyl) terephthalate 1.490 BEETP Bis-(butoxyethoxyethyl) terephthalate 1.487 EETP Bis-(ethoxyethyl) terephthalate 1.497 EEETP Bis-(ethoxyethoxyethyl) terephthalate 1.493 2EH1ETP Bis-(2-ethylhexyloxyethyl) terephthalate 1.483 2EHIP Bis-(2-ethylhexyl) iso-phthalate 1.486 2EH2ETP Bis-(2-ethylhexyloxyethoxyethyl) terephthalate nd 2EHEBz 2-ethylhexyloxyethyl benzoate 1.442 2EHEEBz 2-ethylhexyloxyethoxylethyl benzoate 1.483 EEEBz Ethoxyethoxyethyl benzoate 1.491 BEEBz Butoxyethoxyethyl benzoate 1.487 BEEEBz Butoxyethoxyethoxyethyl benzoate 1.489 DodBz Dodecyl benzoate 1.489 DPGDT Dipropylene glycol di-o-toluate 1.527 TEGBzAc Triethylene glycol benzoate acetate 1.498 Benzoflex 9-88 (B9-88) dipropylene glycol dibenzoate 1.528 Benzoflex B1046 (B1046) 2,2,4-trimethyl-1,3-pentanediol benzoate isobutyrate 1.492 Benzoflex (B2088) Mixure of benzoic acid esters of DPG and DEG 1.538 Benzoflex B131 (B131) Isodecyl benzoate 1.488 Benzoflex B181 (B181) 2-ethylhexyl benzoate 1.489 Uniplex 400 (U400) Polypropylene glycol dibenzoate 1.515-1.520 Benzoflex B354 (B354) 2,2,4-trimethyl-1,3-pentanediol dibenzoate 1.529 Benzoflex B284 (B284) Propylene glycol dibenzoate 1.544 Benzoflex B2-45 (B2-45) Diethylyene glycol dibenzoate 1.542 Surfonc N-40 Nonylphenyl tetraethylene glycol 1.5 

TABLE 16 Interlayer Construction skin layer/core layer/skin layer Skin layer Core Layer Residual Residual Refractive Residual hydroyxl acetate Plasticizer index of Stability of hydroyxl Multilayer Disclosed content content content Resin Layer the Resin Disclosed content Interlayer Interlayer (wt. %) (wt. %) (phr) (nD25) Layer Interlayer (wt. %) DI-42 DL-38 19 <2 38 1.490 exuded DL-43 11 DI-43 DL-39 19 <2 42 1.490 exuded DL-44 11 DI-44 DL-40 19 <2 48 1.489 exuded DL-45 11 DI-45 DL-41 19 <2 54 1.489 exuded DL-46 11 DI-46 DL-42 19 <2 60 1.486 exuded DL-47 11 Delta Core Layer Refractive Residual Refractive Index acetate Plasticizer index of Stability of (skin − Interlayer/ Multilayer content content Resin Layer the Resin core) Laminate Interlayer (wt. %) (phr) (nD25) Layer (nD25) Mottle Stability DI-42 <2 60 1.486 exude 0.004 <1 exuded DI-43 <2 70 1.487 exude 0.003 <1 exuded DI-44 <2 80 1.486 exude 0.004 <1 exuded DI-45 <2 90 1.486 exude 0.003 <1 exuded DI-46 <2 100 1.486 exude 0.000 <1 exuded

As shown in Table 16, the di-2-ethylhexylterephthalate (DOTP) plasticizer used in poly(vinyl acetal) Disclosed Interlayers, DL-38 through DL-47, formed sheets with high refractive indices but the layers were not stable. Over time, the plasticizer exuded from the Disclosed Interlayers and Disclosed Multilayer Interlayers, resulting in the Disclosed Interlayers and Disclosed Multilayer Interlayers being under plasticized, which diminished the acoustic performance. Such exudation can also cause contamination and handling issues. Dioctyl phthalate (DOP) and diisononyl phthalate (DINP) are additional high refractive index plasticizers that are effective in reducing the difference of refractive index between the skin and core layers in the multiple layer interlayers but these multiple layer interlayers are not stable and will exude from the Disclosed Interlayers and are unable to impart the necessary acoustic and mechanical properties. Novel plasticizers that have both a high refractive index and are compatible with the poly(vinyl acetal) resins when formed into Interlayers and Multilayer Interlayers are designed, synthesized, and examined in Examples 12 to 18. Names, respective abbreviations, and refractive indices as measured by nD25 of novel plasticizers are listed in Table 15 along with commercially available plasticizers examined in this invention.

Example 12 General Synthetic Procedure of Terephthalate, Benzoate, and Mixed Benzoic Plasticizers with High Refractive Index

To a 4-neck 2 liter round bottom flask was charged with either dimethyl terephthalate or methyl benzoate (limiting reactant) and an excess of the transesterification alcohol. Titanium isopropoxide catalyst was then added to the mixture. The round bottom was fitted with a Dean-Stark trap and a simple distillation head, which acted as the condenser for the process. A nitrogen sweep was established through the round bottom and condenser. Overhead stirring distributed pot materials evenly throughout the reactions. Reaction temperatures were controlled via a Camile system. Desired temperatures varied depending on the boiling points of starting materials, e.g., about 140° C. to 240° C. The reaction was monitored by GC analysis. Once the GC analysis showed complete conversion of the limiting reagent to product with no residual methanol, the product material was treated with base washes using 10% (W/W 100 mL) solution of potassium hydroxide in DI water at 50° C. for approximately 1.5 minutes. A pH of 14 confirmed neutralization of the catalyst and allowed for continuation to the next wash. The next wash solution was a 6% (w/w 100 mL) sodium bicarbonate and DI water solution to remove unreacted starting material. The excess reagent was removed from the mixture under vacuum, heat and nitrogen purge. After removing the excess reagent, the material in the flask could be analyzed by GC to make sure all excess alcohol or ether was removed as desired. The material was filtered through celite under vacuum with a Buchner funnel and a 1 liter vacuum flask. The final product was weighed, placed in a sample bottle, and distributed for future experimental purposes.

Modifications to this procedure for the various plasticizer molecules synthesized were made due to experimental conditions and relative reactivities.

Example 13 Terephthalic Acid Based Plasticizers with High Refractive Index

Several poly(vinyl acetal) Comparative Interlayers, referred to as CL-20 through CL-22, and several resulting inventive Disclosed Interlayers, referred to as DL-48 through DL-63, are summarized in Table 17. Each of these poly(vinyl butyral) interlayers were formed by mixing one of two poly(vinyl butyral) resins, one with about 19% residual hydroxyl groups and the other with about 11% residual hydroxyl groups, with varying amounts of terephthalic acid based plasticizers such as bis-(methoxyethyl) terephthalate (METP), bis-(butoxyethyl) terephthalate (BETP), bis-(butoxyethoxyethyl) terephthalate (BEETP), bis-(ethoxyethoxyethyl) terephthalate (EEETP), bis-(2-ethylhexyloxyethyl) terephthalate (2EH1 ETP), and bis-(2-ethylhexyloxyethoxyethyl) terephthalate (2EH2ETP) as shown in Table 17. Both the thickness and the refractive index of the PVB Interlayers were measured and summarized in Table 17.

The Comparative and Disclosed Interlayers, CL-20 through CL-22 and DL-48 through DL-63, were then used to create several Comparative and Disclosed Multilayer Interlayers. As explained in Example 3, each multilayer interlayer has a pair of outer “skin” layers sandwiching an inner “core” layer, usually formed of a resin having a lower residual hydroxyl content. The composition and several properties of the multilayer interlayers including refractive index, glass transition temperature, mottle, loss factor, were measured as described above and the results for Comparative Multilayer Interlayers (CI-22 to CI-23) and Disclosed Multilayer Interlayers (DI-57 to DI-62) are summarized in Table 18 below.

TABLE 17 Terephthalic Acid Based Plasticizers Table 15: Terephthalic Acid Based Plasticizers Residual Residual vinyl hydroyxl acetate 3GEH METP BETP BEETP content content content content content content Thickness Refractive Interlayer (wt. %) (wt. %) (phr) (phr) (phr) (phr) EEETP 2EH1ETP 2EH2ETP (mm) Index (nD25) CL-20 19 <2 38 — — — — — — 14 1.477 CL-21 19 <2 38 — — — — — — 5 1.477 CL-22 11 <2 75 — — — — — — 5 1.466 DL-48 19 <2 — 38 — — — — — 14 1.494 DL-49 11 <2 — 75 — — — — — 5 1.494 DL-50 19 <2 — — 41 — — — — 14 1.492 DL-51 19 <2 — — 43 — — — — 14 1.490 DL-52 11 <2 — — 76 — — — — 5 1.486 DL-53 19 <2 — — — 41 — — — 14 1.490 DL-54 19 <2 — — — 43 — — — 14 1.489 DL-55 21 <2 — — — 33 — — — 14 1.490 DL-56 21 <2 — — — 35.5 — — — 14 1.488 DL-57 11 <2 — — — 78 — — — 5 1.486 DL-58 19 <2 — — — — 38 — — 14 1.490 DL-59 11 <2 — — — — 75 — — 5 1.485 DL-60 19 <2 — — — — — 38 — 14 1.492 DL-61 11 <2 — — — — — 75 — 5 1.489 DL-62 19 <2 — — — — — — 38 14 1.493 DL-63 11 <2 — — — — — — 75 5 1.489

TABLE 18 Multilayer Interlayers Glass Transition Delta Refractive Temperature STL at Refractive Index of of Multilayer Reference Index (skin Multilayer Interlayer Loss frequency Multilayer Skin layer − core Interlayer (° C.) Factor at 3,150 Hz Interlayer layer 1 Core Layer Skin layer 2 Plasticizer 1 layer) (nD25) T_(g1) T_(g2) Mottle 20° C. (dB) CI-22 CL-20 CL-21 CL-20 3GEH 0.000 1.477 30 — 0 0.02 31 CI-23 CL-20 CL-22 CL-20 3GEH 0.011 1.475 30 −2 5 0.32 40 DI-47 DL-48 DL-49 DL-48 METP 0.000 1.494 30 0 — — — DI-48 DL-50 DL-52 DL-50 BETP 0.006 1.491 32 1 0.8 0.37 — DI-49 DL-51 DL-52 DL-51 BETP 0.004 1.489 30 1 0.3 0.39 39 DI-50 DL-53 DL-57 DL-53 BEETP 0.004 1.490 29 0 0.5 0.31 38 DI-51 DL-54 DL-57 DL-54 BEETP 0.003 1.490 27 0 0.6 0.35 39 DI-52 DL-55 DL-57 DL-55 BEETP 0.004 1.488 39 0 0.1 0.24 — DI-53 DL-56 DL-57 DL-56 BEETP 0.002 1.489 37 0 0.3 0.28 — DI-54 DL-58 DL-59 DL-58 EEETP 0.005 1.489 32 3 — — — DI-55 DL-60 DL-61 DL-60 2EH1ETP 0.003 1.491 45 17 — — — DI-56 DL-62 DL-63 DL-62 2EH2ETP 0.004 1.493 41 11 — — —

As shown in Table 17 and 18, polyvinyl acetal resins comprising at least one high refractive index plasticizer, including those METP, BETP, BEETP, EEETP, 2EH1ETP, 2EH2ETP plasticizers listed above, tend to exhibit higher refractive indices than those comprising a lower refractive index plasticizer such as triethylene glycol di-2-ethylhexanoate (3GEH). Comparative Multilayer Interlayer CI-22 is a monolithic PVB interlayer, which would behave in the same manner as a trilayer construction of uniform composition (having the same layer composition for each layer). CI-22 has a delta RI of 0 between the interlayers, a single glass transition temperature, no mottle level of 0, little sound damping, and very low or poor sound transmission loss. Comparative Multilayer Interlayer CI-23, which is a multilayer interlayer, has two glass transition temperatures, each corresponding to the respective interlayers. CI-23 exhibits high sound damping and excellent sound transmission loss but also has a high delta RI of 0.011 and a corresponding high mottle of 5. High mottle is objectionable for most multilayer interlayers, particularly those used in applications where good optical properties are critical or necessary. Additionally, as shown by comparison of Disclosed Multilayer Interlayers DI-47 through DI-56, the higher refractive index plasticizer used in the interlayers give a refractive index difference of less than 0.010 exhibited by a low mottle values of 1 or less in addition to excellent damping and sound transmission loss. These corresponding low mottle values were achievable by selecting interlayers having a core layer with a higher or lower refractive index than the skin layer, as long as the absolute value of the difference between the refractive indices of adjacent layers was less than 0.010.

Example 14 Benzoic Acid Based Plasticizers with High Refractive Index

Several benzoic acid based plasticizers are listed by name with their abbreviation and refractive index as measured by nD25 in Table 15 above. These benzoic acid based plasticizers can be mixed with poly(vinyl acetal) resins to produce monolayers, bilayers, and trilayers. The high refractive index demonstrated by these benzoic acid based plasticizers, combined with the ability for greater uptake of these plasticizers by the poly(vinyl acetal) resins with a lower residual hydroxyl content, can be used minimize the difference in refractive indices for the core and skin layers resulting in a less optical defects.

Ethoxyethoxyethyl benzoate (EEEBz), butoxyethoxyethyl benzoate (BEEBz), butoxyethoxyethoxyethyl benzoate (BEEEBz), 2-ethylhexyloxyethyl benzoate (2EHEBz), 2-ethyl hexyloxyethoxylethyl benzoate (2EHEEBz), dodecyl benzoate (DodBz), were used to make Disclosed Interlayers DL-64 through DL-75 in Table 19 below and these Disclosed Interlayers were used to make Disclosed Multilayer Interlayers, DI-57 to DI-62, in Table 20 below. Each Disclosed Multilayer Interlayer included a pair of outer “skin” layers, each having a thickness of 14 mils, sandwiching an inner “core” layer, having a thickness of 5 mils, formed by a resin having a lower residual hydroxyl content.

TABLE 19 Benzoate Based Plasticizers Residual Residual vinyl Refractive hydroyxl acetate Plasticizer Index of content content content Interlayer Interlayer (wt. %) (wt. %) Plasticizers (phr) (nD25) CL-20 19 <2 3GEH 38 1.477 DL-64 19 <2 EEEBz 38 1.495 DL-65 19 <2 BEEBz 30 1.491 DL-66 19 <2 BEEEBz 30 1.492 DL-67 19 <2 2EHEBz 38 1.493 DL-68 19 <2 2EHEEBz 38 1.493 DL-69 19 <2 DodBz 38 1.490 CL-22 11 <2 3GEH 75 1.466 DL-70 11 <2 EEEBz 75 1.493 DL-71 11 <2 BEEBz 60 1.489 DL-72 11 <2 BEEEBz 60 1.488 DL-73 11 <2 2EHEBz 75 1.490 DL-74 11 <2 2EHEEBz 75 1.489 DL-75 11 <2 DodBz 75 1.486

TABLE 20 Multilayer Interlayers with Benzoate Plasticizers Glass Glass Delta Refractive Transition Transition refractive index of Temperature Temperature Multilayer index (skin − interlayer of skin layers of core Interlayer Skin layer 1 Core Layer Skin layer 2 Plasticizer core) (nD25) (° C.) layers (° C.) CI-22 CL-20 CL-21 CL-20 3GEH 0.000 1.477 30 — CI-23 CL-20 CL-22 CL-20 3GEH 0.011 1.475 30 −2 DI-57 DL-64 DL-70 DL-64 EEEBz 0.002 1.493 31 1 DI-58 DL-65 DL-71 DL-65 BEEBz 0.002 1.491 29 −6 DI-59 DL-66 DL-72 DL-66 BEEEBz 0.004 1.491 31 −2 DI-60 DL-67 DL-73 DL-67 2EHEBz 0.003 1.493 31 −3 DI-61 DL-68 DL-74 DL-68 2EHEEBz 0.004 1.493 33 −1 DI-62 DL-69 DL-75 DL-69 DodBz 0.004 1.489 32 −4

As shown in Table 19 and 20, polyvinyl acetal resins comprising at least one high refractive index benzoate plasticizer, including those EEEBz, BEEBz, BEEEBz, 2EHEBz, 2EHEEBz, and DodBz plasticizers listed above, tend to exhibit higher refractive indices than those comprising a lower refractive index plasticizer such as triethylene glycol di-2-ethylhexanoate (3GEH). Additionally, as shown by comparison of Disclosed Multilayer Interlayers DI-57 through DI-62, the higher refractive index plasticizers used in these interlayer sheets give a refractive index difference of less than 0.010. The refractive index of the Disclosed Multilayer Interlayers, DI-57 through DI-62, as measured by nD25 was at least 1.485 for all of the benzoate plasticizers and above 1.490 for the EEEBz, BEEBz, BEEEBz, 2EHEBz, and 2EHEEBz benzoate plasticizers. The glass transition temperature of the core layers using the EEEBz, BEEBz, BEEEBz, 2EHEBz, 2EHEEBz, and DodBz plasticizers all remained at 1° C. or less.

Example 15 Mixed Benzoic Acid Based and Toluate Plasticizers with a High Refractive Index

Several mixed benzoic acid based plasticizers are listed by name with their abbreviation and refractive index as measured by nD25 in Table 15 above. These mixed benzoic acid based plasticizers and toluate plasticizers can be mixed with poly(vinyl acetal) resins to produce monolayers, bilayers, and trilayers. The high refractive index demonstrated by these mixed benzoic acid and toluate based plasticizers, combined with the ability for greater uptake of these plasticizers by the poly(vinyl acetal) resins with a lower residual hydroxyl content, can help minimize the difference in refractive indices between the core and skin layers resulting in a less optical defects.

Dipropylene glycol di-o-toluate (DPGDT) and triethylene glycol benzoate acetate (TEGBzAc) were used to make Disclosed Interlayers DL-76 through DL-79 in Table 21 below and these Disclosed Interlayers were used to make Disclosed Multilayer Interlayers, DI-63 and DI-64, in Table 22 below. Each Disclosed Multilayer Interlayers included a pair of outer “skin” layers, each having a thickness of 14 mils, sandwiching an inner “core” layer, having a thickness of 5 mils, formed by a resin having a lower residual hydroxyl content.

TABLE 21 Mixed Benzoic Acid Based Plasticizers Residual Residual vinyl Refractive hydroyxl acetate Plasticizer index of content content content Interlayer Interlayer (wt. %) (wt. %) Plasticizers (phr) (nD25) CL-20 19 <2 3GEH 38 1.477 DL-76 19 <2 DPGDT 38 1.497 DL-77 19 <2 TEGBzAc 30 1.490 CL-22 11 <2 3GEH 75 1.466 DL-78 11 <2 DPGDT 75 1.500 DL-79 11 <2 TEGBzAc 60 1.489

As shown in Tables 21 and 22, the poly(vinyl acetal) Disclosed Interlayers and Disclosed Multilayer Interlayers mixed with either the DPGDT or TEGBzAc mixed benzoate plasticizer resulted in a refractive index of at least 1.485 for the interlayer and resulting multilayer interlayer. These refractive index values greater than 1.485 or 1.490 for the poly(vinyl acetal) Disclosed Interlayers and Disclosed Multilayer Interlayers using DPGDT or TEGBzAc are relatively higher than the both poly(vinyl acetal) Comparative Interlayers and Comparative Multilayer Interlayers utilizing 3GEH.

TABLE 22 Multilayer Interlayers with Mixed Benzoic Acid Based Plasticizers Glass Glass Delta Refractive Transition Transition refractive index of Temperature Temperature Multilayer index (skin − interlayer of skin layers of core Interlayer Skin layer 1 Core Layer Skin layer 2 Plasticizer core) (nD25) (° C.) layers (° C.) CI-22 CL-20 CL-21 CL-20 3GEH 0.000 1.477 30 — CI-23 CL-20 CL-22 CL-20 3GEH 0.011 1.475 30 −2 DI-63 DL-76 DL-79 DL-76 DPGDT −0.003 1.493 36 8 DI-64 DL-77 DL-80 DL-77 TEGBzAc 0.001 1.489 32 5

Example 16 Varying Core Layer Compositions with High Refractive Index Plasticizers

Several different poly(vinyl butyral) resins or core layer compositions were used to vary both the weight percent of residual hydroxyl content and residual vinyl acetate in the polymer composition. Triethylene glycol di-2-ethylhexanoate (3GEH) and bis-(butoxyethoxyethyl) terephthalate (BEETP) were the plasticizers added in different amounts to these core layer compositions to make Disclosed Interlayers DL-80 to DL-82. Again, the high refractive index demonstrated by these terephthalate plasticizers, combined with the ability for greater uptake of these plasticizers by the poly(vinyl acetal) resins with a lower residual hydroxyl content, can help minimize the difference in refractive indices for the core and skin layers resulting in a less optical defects. The Comparative Interlayers, CL-20 to CL-24, and Disclosed Interlayers, DL-80 to DL-82, in Table 23 below were used to make Comparative Multilayer Interlayers, CI-22 to CI-25, and Disclosed Multilayer Interlayers, DI-65 and DI-66, in Table 24 below. Each multilayer interlayer included a pair of outer “skin” layers, each having a thickness of 14 mils, sandwiching an inner “core” layer, having a thickness of 5 mils, formed by a resin having a lower residual hydroxyl content.

TABLE 23 Plasticizers Mixed with Different Core Layer Compositions Residual Total Residual vinyl plasticizer hydroyxl acetate 3GEH BEETP content in content content content content each layer Refractive Interlayer (wt. %) (wt. %) (phr) (phr) (phr) Index (nD25) CL-20 19 <2 38 — 38 1.477 CL-21 19 <2 38 — 38 1.477 CL-22 11 <2 75 — 75 1.466 CL-23 12 18 75 — 75 1.464 CL-24 12 12 75 — 75 1.465 DL-80 19 <2 — 38 38 1.477 DL-81 12 18 — 75 75 1.487 DL-82 12 12 — 75 75 1.488

TABLE 24 Multilayer Interlayers with Different Core Compositions Delta Refractive Refractive Index of Glass Transition Index (skin Multilayer Temperature Multilayer layer − core Interlayer (° C.) Loss Factor Interlayer Skin layer 1 Core Layer Skin layer 2 Plasticizer 1 layer) (nD25) Skin layer Core layer at 20° C. CI-22 CL-20 CL-21 CL-20 3GEH 0.000 1.477 30 — 0.02 CI-23 CL-20 CL-22 CL-20 3GEH 0.011 1.475 30 −2 0.32 CI-24 CL-20 CL-23 CL-20 3GEH n/a n/a 30 −4 0.36 CI-25 CL-20 CL-24 CL-20 3GEH n/a n/a 36.4 −3 0.31 DI-65 DL-80 DL-81 DL-80 BEETP n/a n/a 38.4 0 0.52 DI-66 DL-80 DL-82 DL-80 BEETP n/a n/a 37.2 1 0.54

As shown in Table 23 and 24, a glass transition temperature lower than 2° C. can be achieved with different poly(vinyl acetal) resins. Additionally, poly(vinyl acetal) resins with different residual hydroxyl and residual acetate content can be used to design interlayers and multilayer interlayers for low glass transition temperatures to improve acoustic and material properties such as sound transmission loss (STL).

Example 17 Making Resin Blends with High Refractive Index Plasticizers

Two polyvinyl n-butyral resins, Resin R-1 and Resin R-2, were prepared according to the procedure described above in Example 1. Resin R-1 had a residual hydroxyl content of 19 weight percent, while resin R-2 had a residual hydroxyl content of 11 weight percent. Both resins had residual acetate contents of 2 weight percent. Several resin blends were prepared that included varying amounts of resins R-1 and R-2 in order to simulate various blending rates. To create the several blends presented in Table 25 to Table 31, Resin R-1 and Resin R-2 are mixed together and plasticizer is added into the mixture and blended together. These components are fed into a Brabender lab melt mixer and melt mixed at a temperature of 170° C. for 7 minutes. The resulting melt is taken out and pressed into a sheet having a thickness of about 0.76 mm in order to form resin layer samples that are then analyzed for Tan Delta, glass transition temperature, HLD Haze, and refractive index as previously described.

Bis-(butoxyethyl) terephthalate (BETP), bis-(ethoxyethyl) terephthalate (EETP), dipropylene glycol di-o-toluate (DPGDT), triethylene glycol benzoate acetate (TEGBzAc), butoxyethoxyethyl benzoate (BEEBz), dodecyl benzoate (DodBz), Bis-(ethoxyethoxyethyl) terephthalate (EEETP), bis-(methoxyethyl) terephthalate (METP), bis-(butoxyethoxyethyl) terephthalate (BEETP), were used to make each of the respective Disclosed Blended Layer DBL-29 through DBL-69 in Tables 25 to Table 31 below. Disclosed Interlayers, DL-83 through DL-140, were additionally made to compare the Tan Delta, glass transition temperature, HLD Haze, and refractive index for additional single resin Disclosed Interlayers.

TABLE 25 Resin Blends and Interlayers with Bis-(butoxyethyl) terephthalate (BETP) Plasticizer Resin R-1 Resin R-2 BETP Tg phr HLD Interlayer (g) (g) (g) (° C.) of pz Haze RI DL-83 50 0 15 40 30 0.56 1.4915 DL-84 50 0 19 33.7 38 0.27 1.4913 DL-85 50 0 21.5 30.3 43 0.49 1.4910 DL-86 0 40 28 5.7 70 1.35 1.4870 DL-87 0 40 30 3.3 75 0.17 1.4867 DL-88 0 40 34 −0.3 85 0.33 1.4866 DBL-29 48 2 17.5 40.1 35 0.84 1.4898 DBL-30 48 2 20 32.5 40 1.01 1.4902 DBL-31 48 2 22.5 29.5 45 1.16 1.4904 DBL-32 2 48 17.5 26.1 35 0.86 1.4870

TABLE 26 Resin Blends and Interlayers with Bis-(ethoxyethyl) terephthalate (EETP) and Bis-(butoxyethyl) terephthalate (BETP) Plasticizer Resin R-1 Resin R-2 HLD Interlayer (g) (g) EETP (g) BETP (g) phr of pz Tg (° C.) tan Delta Haze DL-89 50 0 15 0 30 37 1.424 0.15 DL-90 50 0 19 0 38 28.2 1.28 0.26 DL-91 50 0 21.5 0 43 25.1 1.209 0.41 DL-92 0 40 28 0 70 3.76 1.487 0.3 DL-93 0 40 30 0 75 −0.48 1.34 0.23 DL-94 0 40 34 0 85 −2.68 1.295 0.1 DBL-33 48 2 17.5 0 35 32.3 1.275 0.67 DBL-34 48 2 20 0 40 28.3 1.311 0.7 DBL-35 48 2 22.5 0 45 25.9 1.149 0.57 DBL-36 48 2 0 17.5 35 34.5 1.347 0.75 DBL-37 48 2 0 20 40 31.3 1.189 0.49 DBL-38 48 2 0 22.5 45 29.1 1.104 0.9

TABLE 27 Resin Blends and Interlayer with Dipropylene glycol di-o- toluate (DPGDT) Plasticizer Resin R-1 Resin R-2 HLD Interlayer (g) (g) DPGDT (g) 3GEH (g) phr of pz RI Haze Tg (° C.) tan Delta DL-95 50 0 15 0 30 1.4974 0.28 41.8 1.53 DL-96 50 0 19 0 38 1.4990 0.09 35.7 1.36 DL-97 50 0 21.5 0 43 1.4998 0.31 31.8 1.34 DL-98 0 40 28 0 70 1.5000 0.54 9.2 1.52 DL-99 0 40 30 0 75 1.5005 0.38 7.7 1.52 DL-100 0 40 34 0 85 1.5033 0.98 4.4 1.47 DBL-39 48 2 17.5 0 35 1.4981 0.57 38.3 1.38 DBL-40 48 2 20 0 40 1.4989 0.41 34.3 1.29 DBL-41 48 2 22.5 0 45 1.4996 0.66 30.3 1.24 CL-25 0 40 0 30 75 1.4653 nd −5.4 1.11

TABLE 28 Resin Blends and Interlayers with Triethylene glycol benzoate acetate (TEGBzAc) Plasticizer Resinz Resin R-1 R-2 TEGBzAc phr Tg HLD Interlayer (g) (g) (g) of pz (° C.) tan Delta Haze DL-101 50 0 15 30 31.8 1.4 0.05 DL-102 50 0 19 38 24.9 1.27 0.04 DL-103 50 0 21.5 43 22 1.19 0.00 DL-104 0 40 26 65 3.4 1.31 0.03 DL-105 0 40 30 75 −0.8 1.25 0.10 DL-106 0 40 34 85 −3 1.15 0.04 DBL-42 48 2 17.5 35 28 1.29 0.18 DBL-43 48 2 20 40 24 1.22 0.52 DBL-44 48 2 22.5 45 20.1 1.17 0.36

TABLE 29 Resin Blends and Interlayers with Butoxyethoxyethyl benzoate (BEEBz) and Dodecyl benzoate (DodBz) Plasticizers Resin R-1 Resin R-2 Interlayer (g) (g) DodBz (g) BEEBZ (g) 3GEH (g) Total phr Tg/° C. RI HLD Haze DL-107 50 0 15 0 0 30 37.7 1.4898 0 DL-108 50 0 19 0 0 38 32.3 1.4897 0 DL-109 50 0 21.5 0 0 43 28.6 1.4894 0.03 DL-110 0 40 26 0 0 65 −0.2 1.4868 0.25 DL-111 0 40 30 0 0 75 −4.1 1.4857 0.03 DL-112 0 40 34 0 0 85 −8.9 1.4851 0.38 DBL-45 48 2 17.5 0 0 35 35.2 1.4897 0.81 DBL-46 48 2 20 0 0 40 31.1 1.4876 0.93 DBL-47 48 2 22.5 0 0 45 28.3 1.4890 1.16 DL-113 50 0 0 15 0 30 28.5 1.4910 0 DL-114 50 0 0 19 0 38 22.8 1.4917 0 DL-115 50 0 0 21.5 0 43 19.2 1.4891 0.08 DL-116 0 40 0 26 0 65 −7.9 1.4878 0 DL-117 0 40 0 30 0 75 −14.1 1.4857 0.08 DL-118 0 40 0 34 0 85 −15.1 1.4891 0.31 DBL-48 48 2 0 17.5 0 35 23.5 1.4928 0.27 DBL-49 48 2 0 20 0 40 19.8 1.4934 0.33 DBL-50 48 2 0 22.5 0 45 16.3 1.4933 0.48 DBL-51 25 25 21.5 0 0 43 34.5 1.4907 14.3 DBL-52 25 25 0 21.5 0 43 21.6 1.4922 5.0 CL-26 25 25 0 0 21.5 43 33.7 1.4767 67.4

TABLE 30 Resin Blends with Bis-ethoxyethoxyethyl terephthalate (EEETP), Bis-methoxyethyl terephthalate (METP), and Bis- butoxyethoxyethyl terephthalate (BEETP) Plasticizers Resin R-1 Resin R-2 BEETP Interlayer (g) (g) (g) EEETP (g) METP 3GEH (g) Total phr Tg/° C. HLD Haze RI DL-119 50 0 15 0 0 0 30 38.5 0 1.4934 DL-120 50 0 19 0 0 0 38 32 0 1.4931 DL-121 50 0 21.5 0 0 0 43 28.8 0.46 1.4913 DL-122 0 40 26 0 0 0 65 6.5 0.09 1.4888 DL-123 0 40 30 0 0 0 75 1 0.13 1.4888 DL-124 0 40 34 0 0 0 85 −1.5 0 1.4862 DBL-53 48 2 17.5 0 0 0 35 35.3 0.38 1.4917 DBL-54 48 2 20 0 0 0 40 31.7 0.63 1.4927 DBL-55 48 2 22.5 0 0 0 45 27.6 0.56 1.4917 DL-125 50 0 0 15 0 0 30 36.8 0.02 1.4945 DL-126 50 0 0 19 0 0 38 31.4 0.12 1.4965 DL-127 50 0 0 21.5 0 0 43 27.1 0.21 1.4965 DL-128 0 40 0 26 0 0 65 4.7 0.31 1.4899 DL-129 0 40 0 30 0 0 75 0.8 0.09 1.4899 DL-130 0 40 0 34 0 0 85 — 0.53 — DBL-56 48 2 0 17.5 0 0 35 — 0.48 1.4928 DBL-57 48 2 0 20 0 0 40 — 0.16 1.4942 DBL-58 48 2 0 22.5 0 0 45 — 0.70 1.4918 DL-131 50 0 0 0 15 0 30 36.2 0 1.4980 DL-132 50 0 0 0 19 0 38 29.5 0.02 1.4942 DL-133 50 0 0 0 21.5 0 43 25.4 0 1.4999 DL-134 0 40 0 0 26 0 65 4.8 0 1.4951 DL-135 0 40 0 0 30 0 75 0 0.06 1.4938 DL-136 0 40 0 0 34 0 85 −2.4 0.44 1.4951 DBL-59 48 2 0 0 17.5 0 35 31.5 0.20 1.4979 DBL-60 48 2 0 0 20 0 40 27.2 0.16 1.4948 DBL-61 48 2 0 0 22.5 0 45 24.2 0.46 1.4931 DBL-62 25 25 21.5 0 0 0 43 1.8, 37.1 12.66 1.4848 DBL-63 25 25 0 21.5 0 0 43 10.0, 27.1 5.55 1.4900 DBL-64 25 25 0 0 21.5 0 43 12.2, 26.5 4.06 1.4937 CL-27 25 25 0 0 0 21.5 43 −4.1, 38.9 125.78 1.4753

Example 18 Making Resin Blend Sheets with High Refractive Index Plasticizers

Two polyvinyl n-butyral resins, Resin R-1 and Resin R-2, were prepared according to the procedure described above in Example 1. Resin R-1 had a residual hydroxyl content of 19 weight percent, while resin R-2 had a residual hydroxyl content of 11 weight percent. Both resins had residual acetate contents of 2 weight percent. These components are fed into a Brabender lab melt mixer and melt mixed at a temperature of 170° C. for 7 minutes. The resulting melt is taken out and pressed into a sheet having a thickness of about 30 guage in order to form resin layer samples. Two resin layers were prepared for each of the triethylene glycol di-2-ethylhexanoate (3GEH), bis-(butoxyethyl) terephthalate (BETP), bis-(butoxyethoxyethyl) terephthalate (BEETP), butoxyethoxyethyl benzoate (BEEBz), dodecyl benzoate (DodBz) plastcizers. The first layer was entirely Resin R-1 with the respective plasticizer and the second layer was 96 parts Resin R-1 and 4 parts Resin R-2 with the same respective plasticizer. The resin layer samples were analyzed for Haze and Visible light transmittance.

TABLE 31 Sheets of Resin Blends with Plasticizer Sheet Composition and Property 3GEH BETP BEETP BEEBz DodBz PVB sheet No. CL-28 CBL-18 DL-137 DBL-65 DL-138 DBL-66 DL-139 DBL-67 DL-140 DBL-68 Parts by wt. PVB Resin R-1 100 96 100 96 100 96 100 96 100 96 Parts by wt. PVB Resin R-2 0 4 0 4 0 4 0 4 0 4 plasticizer content (phr) 40 40 40 40 40 40 40 40 40 40 Haze (%) 0.3 1.9 0.3 0.4 0.4 0.4 0.4 0.4 0.3 0.4 Visible light transmittance (%) 87.8 84.6 87.8 87.7 87.7 87.9 88 87.8 87.8 87.6

As shown in Table 31, above, blended poly(vinyl acetal) resin layers or interlayers formed with 3GEH exhibit increased optical defects, as indicated by a haze percentage greater than 1. The blended poly(vinyl acetal) resin layer or interlayer formed with BETP, BEETP, BEEBz, and DodBz, DBL-65 through DBL-68, exhibit less optical defects as indicated by a haze percentage less than 1. Additionally, the blended poly(vinyl acetal) Disclosed Interlayers formed with BETP, BEETP, BEEBz, and DodBz, DBL-65 through DBL-68, have the same haze value as the single resin poly(vinyl acetal) Disclosed Interlayers DL-137 through DL-140. The blended poly(vinyl acetal) Disclosed Interlayers formed with BETP, BEETP, BEEBz, and DodBz show less of a difference in visible light transmittance than the CL-28 and CBL-18 examples using 3GEH.

While the invention has been disclosed in conjunction with a description of certain embodiments, including those that are currently believed to be the preferred embodiments, the detailed description is intended to be illustrative and should not be understood to limit the scope of the present disclosure. As would be understood by one of ordinary skill in the art, embodiments other than those described in detail herein are encompassed by the present invention. Modifications and variations of the described embodiments may be made without departing from the spirit and scope of the invention

It will further be understood that any of the ranges, values, or characteristics given for any single component of the present disclosure can be used interchangeably with any ranges, values or characteristics given for any of the other components of the disclosure, where compatible, to form an embodiment having defined values for each of the components, as given herein throughout. For example, an interlayer can be formed comprising poly(vinyl butyral) having a residual hydroxyl content in any of the ranges given in addition to comprising a plasticizers in any of the ranges given to form many permutations that are within the scope of the present disclosure, but that would be cumbersome to list. Further, ranges provided for a genus or a category, such as phthalates or benzoates, can also be applied to species within the genus or members of the category, such as dioctyl terephthalate, unless otherwise noted. 

What is claimed is:
 1. A blended resin composition comprising: a first poly(vinyl acetal) resin comprising a residual hydroxyl content; a second poly(vinyl acetal) resin comprising a residual hydroxyl content; and at least one plasticizer having a refractive index of at least 1.460 to about 1.520; wherein the residual hydroxyl content of said second poly(vinyl acetal) resin is at least 2 weight percent lower than the residual hydroxyl content of said first poly(vinyl acetal) resin, wherein said first poly(vinyl acetal) resin comprises residues of a first aldehyde and said second poly(vinyl acetal) resin comprises residues of a second aldehyde, and wherein said first and said second aldehydes have the same number of carbon atoms per molecule, wherein said second poly(vinyl acetal) resin is present in said blended resin composition in an amount of from about 2.2 weight percent to about 11.1 weight percent, based on the total weight of said first and said second poly(vinyl acetal) resins, and wherein said blended resin composition has a haze value of 0.6 or less; wherein the residual hydroxyl content of said first poly(vinyl acetal) resin is in the range of from about 18 to about 22 weight percent, wherein the residual hydroxyl content of said second poly(vinyl acetal) resin is in the range of from about 10 to about 13 weight percent, wherein said first poly(vinyl acetal) resin has a residual acetate content and said second poly(vinyl acetal) resin has a residual acetate content, wherein the residual acetate contents of said first and said second poly(vinyl acetal) resins are each not more than 2 weight percent, and wherein said plasticizer is present in said blended resin composition in an amount in the range of from about 35 to about 45 phr.
 2. The blended resin composition of claim 1, wherein said blended resin composition has a refractive index of at least 1,485.
 3. The blended resin composition of claim 1, wherein said plasticizer has a refractive index in the range of from 1.485 to 1.506, and wherein said blended resin composition has a percent visual transmittance of at least 88 percent.
 4. The blended resin composition of claim 1, wherein said plasticizer comprises a blend of two or more plasticizers.
 5. The blended resin composition of claim 1, wherein said blended resin composition has a refractive index of at least 1.492, wherein said plasticizer has a refractive index in the range of from 1.485 to 1.506, wherein said blended resin composition has a percent visual transmittance of at least 88 percent.
 6. The blended resin composition of claim 1, wherein said first and said second aldehydes comprise butyraldehyde, and wherein said plasticizer is selected from the group consisting of dioctyl phthalate, a mixture of benzoic acid esters of dipropylene glycol (DPG) and diethylene glycol (DEG), and nonylphenyl tetraethylene glycol.
 7. The blended resin composition of claim 1, wherein said first aldehyde and said second aldehyde comprise butyraldehyde, wherein the residual hydroxyl content of said first poly(vinyl acetal) resin is in the range of from about 18 to about 22 weight percent, wherein the residual hydroxyl content of said second poly(vinyl acetal) resin is in the range of from about 10 to about 13 weight percent, wherein said first poly(vinyl acetal) resin has a residual acetate content and said second poly(vinyl acetal) resin has a residual acetate content, wherein the residual acetate contents of said first and said second poly(vinyl acetal) resins are each not more than 2 weight percent, wherein said plasticizer has a refractive index in the range of from 1.485 to 1.506 and is selected from the group consisting of dioctyl phthalate, a mixture of benzoic acid esters of dipropylene glycol (DPG) and diethylene glycol (DEG), and nonylphenyl tetraethylene glycol, wherein said plasticizer is present in said blended resin composition in an amount in the range of from about 35 to about 45 phr, wherein said blended resin composition has a refractive index of at least 1.492 and a percent visual transmittance of at least 88 percent. 